Naslov:Effect of residual stresses on the fatigue crack propagation in welded joints
Avtorji:Gubeljak, Nenad (Avtor)
Predan, Jožef (Avtor)
Pippan, Reinhard (Avtor)
Oblak, Maks (Avtor)
Datoteke:URL http://dx.doi.org/10.1520/JAI12036
 
Jezik:Angleški jezik
Vrsta gradiva:Neznano ()
Tipologija:1.01 - Izvirni znanstveni članek
Organizacija:FS - Fakulteta za strojništvo
Opis:The effect of residual stress on the fatigue crack growth was investigated forcyclic tension. Three-point bend specimens were used with through thicknessnotches at the center line of the welded joint. The experiments were performed for different load amplitudes and load ratios under conditions of small-scale yielding. The influence of the residual stresses on fatigue crack growth was estimated by experimentally observed fatigue crack growth rate and measurement of residual stresses at the surface of specimen. This paper describes an approach taken in two models to estimate the residual stress effect on fatigue crack propagation and to predict remaining service life of awelded structure.
Ključne besede:fracture mechnaics, fatigue crack, crack growth, residual stresses, fatigue crack growh rate, X-ray
Leto izida:2005
UDK:539.42:620.17
COBISS_ID:9785878 Povezava se odpre v novem oknu
ISSN pri članku:Y505-8627
NUK URN:URN:SI:UM:DK:ST1BIYME
Število ogledov:1160
Število prenosov:53
Metapodatki:XML RDF-CHPDL DC-XML DC-RDF
Področja:Ostalo
:
  
Skupna ocena:(0 glasov)
Vaša ocena:Ocenjevanje je dovoljeno samo prijavljenim uporabnikom.
Objavi na:AddThis
AddThis uporablja piškotke, za katere potrebujemo vaše privoljenje.
Uredi privoljenje...

Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše podrobnosti ali sproži prenos.

Gradivo je del revije

Naslov:Journal of ASTM International
Založnik:ASTM International
ISSN:1546-962X
COBISS.SI-ID:9763606 Novo okno

Sekundarni jezik

Jezik:Angleški jezik
Ključne besede:lomna mehanika, utrujenostna razpoka, širjenje razpoke, zaostale napetosti, stopnja rasti razpoke


Komentarji

Dodaj komentar

Za komentiranje se morate prijaviti.

Komentarji (0)
0 - 0 / 0
 
Ni komentarjev!

Nazaj
Logotipi partnerjev Univerza v Mariboru Univerza v Ljubljani Univerza na Primorskem Univerza v Novi Gorici