Avtorji:ID Rak, Inoslav (Avtor)
ID Gliha, Vladimir (Avtor)
Datoteke:URL http://www.dlib.si/details/URN:NBN:SI:doc-ZNTCUCGZ
 
Jezik:Angleški jezik
Vrsta gradiva:Delo ni kategorizirano
Tipologija:1.01 - Izvirni znanstveni članek
Organizacija:FS - Fakulteta za strojništvo
Opis:Under-matched weld joints were adopted for producing a penstock of 47 mm wall thickness and 4200 mm diameter, to improve the weldability. The isothermal Robertson wide plate test on the under-matched weld joints, were the allowable stress level was 0.6 of the yield stress, proved that the longitudinal stresses caused the crack propagation alog the weld joint to deviate into tough base material where it was arrested. The arrest temperature was between -10 and -20°C. The behaviour of the crack propagation was the reason to omit the thermal stress relieving of the pipe section and on circumferential weld joints executed on this side. One can always take into consideration the role of axial residual stresses when assessing whether to use, or not, under-matched weld joints in severer loaded structures.
Ključne besede:strjeni zvar z nižjo mejo tečenja, zaostale napetosti, potek loma, lastnosti ujetja, lomna žilavost, under-matched weld joint, residual stresses, fracture path, arrest properties, fracture toughness
Založnik:Inštitut za kovinske materiale in tehnologije
Leto izida:1999
Št. strani:str. 437-441
Številčenje:Letn. 33, št. 6
PID:20.500.12556/DKUM-53258 Novo okno
UDK:621.791.05:539.42:539.55
COBISS.SI-ID:203434 Novo okno
ISSN pri članku:1318-0010
NUK URN:URN:SI:UM:DK:CPSABHC8
Datum objave v DKUM:10.07.2015
Število ogledov:1582
Število prenosov:47
Metapodatki:XML DC-XML DC-RDF
Področja:Ostalo
:
RAK, Inoslav in GLIHA, Vladimir, 1999, Role of residual stresses on fracture properties of under-matched butt weld. Kovine zlitine tehnologije [na spletu]. 1999. Vol. 33, no. 6, p. 437–441. [Dostopano 18 marec 2025]. Pridobljeno s: http://www.dlib.si/details/URN:NBN:SI:doc-ZNTCUCGZ
Kopiraj citat
  
Skupna ocena:
0.5
1
1.5
2
2.5
3
3.5
4
4.5
5
(0 glasov)
Vaša ocena:Ocenjevanje je dovoljeno samo prijavljenim uporabnikom.
Objavi na:Bookmark and Share


Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše podrobnosti ali sproži prenos.

Gradivo je del revije

Naslov:Kovine zlitine tehnologije
Skrajšan naslov:Kovine zlit. tehnol.
Založnik:Inštitut za kovinske materiale in tehnologije
ISSN:1318-0010
COBISS.SI-ID:31742209 Novo okno

Sekundarni jezik

Jezik:Angleški jezik
Naslov:Vloga zaostalih napetosti na lomne lastnosti trdnostno nižjega strjenega zvara
Opis:Izbran je bil zvarni spoj z nižjo mejo tečenja v strjenem delu zvara za izdelavo tlačnega cevovoda z debelino stene 47 mm in premerom cevi 4200 mm zaradi izboljšave varivosti. Izotermni Robertsonov preizkus izveden na zvarnem spoju obremenjenem z dopustno napetostjo 0,6 meje tečenja je dokazal, da so vzdolžne zaostale napetosti povzročile odmik širjenja razpoke v žilav osnovni material, kjer se je lom ujel. Temperatura ujetja je bila med -10 in -20°C. To dogajanje je bilo vzrok za izpustitev termičnega popuščanja zaostalih napetosti na sekcijah cevi in radialnih zvarnih spojih izvedenih na montaži. Zaostale vzdolžne napetosti je vedno možno upoštevati pri ocenitvi uporabe strjenega zvara z nižjo mejo tečenja od osnovnega materiala za visoko obremenjene konstrukcije.


Komentarji

Dodaj komentar

Za komentiranje se morate prijaviti.

Komentarji (0)
0 - 0 / 0
 
Ni komentarjev!

Nazaj
Logotipi partnerjev Univerza v Mariboru Univerza v Ljubljani Univerza na Primorskem Univerza v Novi Gorici