Title:VPLIV TERMIČNE OBDELAVE NA LOMNO ŽILAVOST VZMETNEGA JEKLA
Authors:ID Likeb, Andrej (Author)
ID Gubeljak, Nenad (Mentor) More about this mentor... New window
ID Predan, Jožef (Comentor)
Files:.pdf UNI_Likeb_Andrej_2011.pdf (7,70 MB)
MD5: 9EE4A687D301785FF62F4D549F6E6FFA
PID: 20.500.12556/dkum/bde63045-da46-4f49-bb4e-824a6236736c
 
Language:Slovenian
Work type:Undergraduate thesis
Organization:FS - Faculty of Mechanical Engineering
Abstract:Visoko trdnostna jekla se uporabljajo na področjih velikih dinamičnih obremenitev. Zaradi česar se proizvajalci običajno soočajo s težavami, kako zagotoviti trajno dinamično trdnost. Za njeno zagotovitev največkrat posegajo po naknadnih termičnih obdelavah. Namen diplomskega dela je tako narediti primerjalno analizo utrujenostne rasti razpoke v skladu s standardom ASTM E 1820 - 01, za termično mehko in termično obdelano vzmetno jeklo 51CrMOV4. Diplomsko delo temelji na eksperimentalnih meritvah v LSEK laboratoriju na Fakulteti za strojništvo, kjer so se izvajali lomnomehanski preizkusi z metodo mehanike loma, določevale utrujenostne rasti razpoke in materialna parametra Parisovega zakona. Obdelava podatkov je potekala v programu Microsoft Excel 2010, s katerim so tudi bili izrisani diagrami. V diplomskem delu je v splošnem opisana mehanika loma ter področje utrujanja: njeni mehanizmi za nastanek, LCF in HCF utrujanje, določevanje hitrosti rasti razpoke in razni vplivi nastanka. Kratko poglavje v diplomskem delu je namenjeno tudi pripravi upogibnih lomnomehanskih preizkušancev v skladu s standardi.
Keywords:Vzmetno jelko 51CrMoV4, mehanika loma, LCF in HCF utrujanje, lomna žilavost, ASTM E1820 - 05, časovno spremenljivo obremenjevanje, mikromehanizmi utrujanja, širjenje kratkih razpok, ASTM E1820 - 01, Wӧhlerjeva krivulja, mehanske lastnosti, Kitagawa - Takahashijev diagram, Parisov zakon, utrujenostna rast razpoke
Place of publishing:Maribor
Publisher:[A. Likeb]
Year of publishing:2011
PID:20.500.12556/DKUM-19826 New window
UDC:[539.42:620.178]:669.018.259(043.2)
COBISS.SI-ID:15806486 New window
NUK URN:URN:SI:UM:DK:7FJ4OY16
Publication date in DKUM:02.09.2011
Views:4365
Downloads:377
Metadata:XML DC-XML DC-RDF
Categories:KTFMB - FS
:
LIKEB, Andrej, 2011, VPLIV TERMIČNE OBDELAVE NA LOMNO ŽILAVOST VZMETNEGA JEKLA [online]. Bachelor’s thesis. Maribor : A. Likeb. [Accessed 8 April 2025]. Retrieved from: https://dk.um.si/IzpisGradiva.php?lang=eng&id=19826
Copy citation
  
Average score:
0.5
1
1.5
2
2.5
3
3.5
4
4.5
5
(0 votes)
Your score:Voting is allowed only for logged in users.
Share:Bookmark and Share



Similar works from other repositories:

No similar works found

Hover the mouse pointer over a document title to show the abstract or click on the title to get all document metadata.

Secondary language

Language:English
Title:INFLUENCE OF THERMAL TREATMENTS ON FRACTURE TOUGHNESS OF SPRING STEEL
Abstract:High strength steels are used in fields of large dynamic loads. Leading manufacturers are usually confronted with problems like, how to ensure fatigue limit. To ensure, they mostly reach to subsequent thermal treatment. The purpose of Diploma thesis is, to make a comparative analysis of fatigue crack growth, for thermal soft and thermal treathed 51CrMOV4 spring steel in accordance with ASTM E 1820-01 standard. Diploma work is based on experimental measurements in LSEK laboratory at the Faculty of Engineering, where tests are conducted on fracture toughness with prescriptive method of fracture mechanics, determined fatigue crack growth and material parameters for Paris’ law. Processing of the data was held in Microsoft Excel 2010, with which diagrams also were drawn. The Diploma thesis described in the general field of fracture mechanics and fatigue: the mechanism for the formation, LCF and HCF fatigue, crack growth rate determination and the creation fatigue failure by various effects. A short chapter in the thesis is also intended to prepare the bending fracture toughness specimen in accordance with the standards.
Keywords:Spring steel 51CrMOV4, fracture mechanics, LCF and HCF fatigue, fracture toughness, ASTM E1820 - 05, timely variable loading, micromechanisms of fatigue, growth of short cracks, ASTM E1820 - 01, Wӧhler's curve, mechanical properties, Kitagawa - Takahashi diagram, Paris' law, fatigue crack growth


Comments

Leave comment

You must log in to leave a comment.

Comments (0)
0 - 0 / 0
 
There are no comments!

Back
Logos of partners University of Maribor University of Ljubljana University of Primorska University of Nova Gorica