| Naslov: | Comparison of the mechanical properties of hardfacings made by standard coated stick electrodes and a newly developed rectangular stick electrode |
|---|
| Avtorji: | ID Bjelajac, Edvard (Avtor)
ID Skumavc, Andrej (Avtor)
ID Lojen, Gorazd (Avtor)
ID Manjgo, Mirza (Avtor)
ID Vuherer, Tomaž (Avtor) |
|---|
| Datoteke: |  materials-17-02051-v2.pdf (10,82 MB)
MD5: D6E61CB47EAD408AFE41C3DFF61F13E7
 https://www.mdpi.com/1996-1944/17/9/2051
|
|---|
| Jezik: | Angleški jezik |
|---|
| Vrsta gradiva: | Članek v reviji |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: | FS - Fakulteta za strojništvo
|
|---|
| Opis: | Cladding with a stick electrode is one of the oldest arc processes for adding a deposit on a base material. The process is suitable for outdoor working, but the disadvantages are low productivity and large dilution rates. In this work, a simple solution is proposed, which would enable cladding of a larger area with one pass and decrease the dilution rate at the same time—a new type of electrode was developed, exhibiting a rectangular cross-section instead of a round one. Hardfacings, welded with E Fe8 electrodes according to EN 14 700 Standard were welded on mild steel S355 J2 base material with three different coated stick electrodes. The first one was a commercially available, standard, round hardfacing electrode, the second was the same, but with a thinner coating, and the third one was a newly developed rectangular electrode. All three types had equal cross-sections of the metallic core and the same type of coating. Manufacturing of the rectangular electrodes in the laboratory is explained briefly. One- and multi-layer deposits were welded with all three types. Differences were observed in the arc behavior between the round and rectangular electrodes. With the rectangular electrode, the microstructure of the deposit was finer, penetration was shallower, and dilution rates were lower, while the hardness was higher, residual stresses predominantly compressive, and the results of instrumented Charpy impact tests and fracture mechanics tests were better. |
|---|
| Ključne besede: | hardfacing, dilution rate, hardness, Charpy impact toughness, residual stress, fracture toughness |
|---|
| Status publikacije: | Objavljeno |
|---|
| Verzija publikacije: | Objavljena publikacija |
|---|
| Poslano v recenzijo: | 23.04.2024 |
|---|
| Datum sprejetja članka: | 25.04.2024 |
|---|
| Datum objave: | 27.04.2024 |
|---|
| Založnik: | MDPI |
|---|
| Leto izida: | 2024 |
|---|
| Št. strani: | 22 str. |
|---|
| Številčenje: | Vol. 17, iss. 9, [article no.] 2051 |
|---|
| PID: | 20.500.12556/DKUM-88589  |
|---|
| UDK: | 621.791 |
|---|
| COBISS.SI-ID: | 195422979 |
|---|
| DOI: | 10.3390/ma17092051 |
|---|
| ISSN pri članku: | 1996-1944 |
|---|
| Datum objave v DKUM: | 14.05.2024 |
|---|
| Število ogledov: | 298 |
|---|
| Število prenosov: | 26 |
|---|
| Metapodatki: |    |
|---|
| Področja: | Ostalo
|
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Skupna ocena: | (0 glasov) |
|---|
| Vaša ocena: | Ocenjevanje je dovoljeno samo prijavljenim uporabnikom. |
|---|
| Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |