Title:Določitev lomno mehanskih lastnosti na zvarnem spoju zvarjenem z gnetenjem
Authors:Jerčič, Klemen (Author)
Vuherer, Tomaž (Mentor) More about this mentor... New window
Kramberger, Janez (Co-mentor)
Files:.pdf VS_Jercic_Klemen_2016.pdf (3,58 MB)
MD5: C44A60A2C32100F77B680C6DBD355B28
 
Language:Slovenian
Work type:Bachelor thesis/paper (mb11)
Typology:2.11 - Undergraduate Thesis
Organization:FS - Faculty of Mechanical Engineering
Abstract:Cilj moje diplomske naloge je bil, da ugotovim, katere od treh hitrosti varjenja po varjenju z gnetenjem imajo najboljše mehanske lastnosti in najboljšo mehaniko loma ter v katerem območju vara (istosmerno, sredina, protismerno) so najboljše lastnosti. Var in osnovi material smo preizkušali po treh preizkusih. Prvi preizkus je bil natezni preizkus, pri katerem smo testirali osnovni material in var. Rezultate smo med seboj primerjali in ugotovili, da ima najboljše lastnosti osnovni material ter s tem potrdili naša predvidevanja. Drugi preizkus je bil preizkus udarne žilavosti (Charpy kladivo) pri sobni temperaturi. Imeli smo preizkušanec iz osnovnega materiala in iz treh delov vara. Udarna žilavost je bila največja pri osnovnem materialu. Iskali smo tudi, katera od treh hitrosti varjenja (A,B,C) se bo s svojimi lastnostmi najbolj približala osnovnemu materialu. Hitrost B je dala v povprečju najboljše rezultate pri udarni žilavosti in se je najbolj približala osnovnemu materialu. Zadnji preizkus je bil ASTM E1820, kjer smo preverjali, kako dobro se material upira širitvi že nastale razpoke. Preizkus je potekal v treh glavnih korakih: utrujanje, širjenje razpoke in utrujanje do zloma. Pri vsakem koraku smo zabeležili podatke, ki so nam podali končno sliko. Zmerili smo tudi razpoke, ki so nastale v drugem koraku. In na podlagi zbranih podatkov določili, katera od hitrosti se je najbolje obnesla. Najboljše lastnosti je v povprečju dosegla hitrost B. Končni sklep je bil, da ima plošča B najboljše lomno mehanske lastnosti.
Keywords:Varjenje, lomna mehanika, natezni preizkus, udarna žilavost, ASTM E1820
Year of publishing:2016
Publisher:[K. Jerčič]
Source:Maribor
UDC:620.174:621.791.053(043.2)
COBISS_ID:20345878 New window
NUK URN:URN:SI:UM:DK:YHDGWVSP
Views:1144
Downloads:125
Metadata:XML RDF-CHPDL DC-XML DC-RDF
Categories:KTFMB - FS
:
  
Average score:(0 votes)
Your score:Voting is allowed only for logged in users.
Share:AddThis
AddThis uses cookies that require your consent. Edit consent...

Hover the mouse pointer over a document title to show the abstract or click on the title to get all document metadata.

Secondary language

Language:English
Title:Determination of the fracture mechanics properties on FSW welded joint
Abstract:The aim of my thesis was to find out which of the tree speeds (A,B,C) gave me the best results on mechanical properties and fracture mechanics. And in which the sealing zone (in the same direction, centre, opposite) are the best features. Weld joint and the basis of the material was tested in three trials. The first test was a tensile test, in which we tested the base material and weld joint. The results were compared with each other and found that the best properties belong to base material, thus confirming our prediction. The second test was a test of impact strength (Charpy hammer) at room temperature. We had a specimen from the base material and three parts deceiving. Impact toughness was the largest in the base material. We were looking for a one of three welding speeds (A, B, C) will be with their properties closest to the base material. The speed of B has given us an average of the best results in terms of impact toughness and is closest to the base material. The last test was ASTM E1820, which we examined how well the material resists the expansion of cracks. The experiment was carried out in three main steps, fatigue, crack propagation and fatigue to fracture. At each step, we recorded information that we give a final image. We measured the cracks that occurred in the second step. And based on the collected data to determine which of speed performed the best. Best properties reach an average speed B. The conclusion was that the best fracture mechanical properties of the plate B
Keywords:welding, fracture mechanics, tensile test, impact toughness, ASTM E1820


Comments

Leave comment

You have to log in to leave a comment.

Comments (0)
0 - 0 / 0
 
There are no comments!

Back
Logos of partners University of Maribor University of Ljubljana University of Primorska University of Nova Gorica