Fatigue crack growth and fracture mechanics analysis of a working roll surface layer material
Matej Drobne, Tomaž Vuherer, Ivan Samardžić, Srečko Glodež, 2014, izvirni znanstveni članek

Opis: Fatigue crack growth and fracture mechanics analysis of a working roll surface layer material is presented in this paper. The research is done on a hot strip mill working roll where High Chromium Steel is used for roll’s shell material. To obtain corresponding parameters, a rectangular single edge notched bend specimens – SENB, according to standard BS 7448, were used. The fatigue crack growth analysis was done on a resonant testing machine with use of special crack gauges, while for fracture mechanics parameters the electro–mechanical testing machine was used.
Ključne besede: fracture mechanics, fatigue crack growth, metal forming, rolling process, high chromium steel
Objavljeno: 03.07.2017; Ogledov: 301; Prenosov: 60
.pdf Celotno besedilo (1,11 MB)
Gradivo ima več datotek! Več...

Iskanje izvedeno v 0.02 sek.
Na vrh
Logotipi partnerjev Univerza v Mariboru Univerza v Ljubljani Univerza na Primorskem Univerza v Novi Gorici