| | SLO | ENG | Piškotki in zasebnost

Večja pisava | Manjša pisava

Iskanje po katalogu digitalne knjižnice Pomoč

Iskalni niz: išči po
išči po
išči po
išči po
* po starem in bolonjskem študiju

Opcije:
  Ponastavi


1 - 2 / 2
Na začetekNa prejšnjo stran1Na naslednjo stranNa konec
1.
The development of ARM-based portable and adaptable power supply
Tomislav Brlek, 2019, magistrsko delo

Opis: This master’s thesis describes a development of a portable and adjustable power supply. The first part of the thesis introduces us to the working principle of power supplies in general. Next, we present a functional design of a portable and adjustable power supply and a list of its required functionalities. Chapter “switched-mode power supplies” introduces us to the theoretical basics of the said power supplies, while chapter “linear regulators” introduces us to different types of linear regulators and tells us more about how they work. Everything regarding which microcontroller was used and why it was used is described in the “ARM microcontroller” chapter. Besides microcontrollers, it also talks about which integrated development environment is used and how the microcontroller is programmed. A full and detailed description of each part of the analog circuitry can be found in the chapter “describing the development of the portable and adjustable power supply”. Lastly, the user interface is described in detail.
Ključne besede: portable power supply, ARM processor, variable laboratory bench power supply, LCD touchscreen, energy efficient, lithium battery, battery charger, voltage control
Objavljeno: 13.11.2019; Ogledov: 435; Prenosov: 70
.pdf Celotno besedilo (3,85 MB)

2.
Subsolidus phase equilibria and the Li[sub]5Nd[sub]4FeO[sub]10 phase in the Li[sub]2O-Nd[sub]2O[sub]3-Fe[sub]2O[sub]3 system
Irena Ban, Mihael Drofenik, Danilo Suvorov, Darko Makovec, 2005, izvirni znanstveni članek

Opis: A survey of the subsolidus phase equilibria in the system Li2O-Nd2O3-Fe2O3 wasmade at subsolidus temperatures in the range 1000-1050 °C. A ternary phase was identified. The phase is centered on Li5Nd4FeO10, with a cubic lattice a =11.9494 A. The compound melts incongruently at 1105 °C. The magnetic susceptibility was measured in the temperature range 4-300 K. The compound is paramagnetic in the temperature range 150-300 K and follows the Curie-Weiss law. At about TN = 10 K, a long-range magnetic ordering is observed.
Ključne besede: lithium ferrites, differential scanning calorimetry, thermogravimetric analysis, X-ray diffraction, magnetic properties, phase equilibrium
Objavljeno: 01.06.2012; Ogledov: 1642; Prenosov: 24