PB(II) AND HG(II) IONS ADSORPTION USING SURFACE MODIFIED SUPERPARAMAGNETIC IRON OXIDE NANOPARTICLES
2014, doktorska disertacija

Opis: Cobalt ferrite (CoFe2O4) nanoparticles prepared via co-precipitation method were modified with tetraethoxysilane (TEOS) and additional funkcionalized with 3-mercaptopropyl trimethoxysilane (MPTMS) with purpose of cleaning waste water contaminated with heavy metal ions (Pb2+ and Hg2+). The influence of different experimental parameters (reaction time, reaction temperature and different TEOS:MPTMS ratios) on silica coating of CoFe2O4 nanoparticles and additional on thiol group was systematically studied. Silanes adsorb to the particle surface with alkoxy (Si(OR)4) groups at one end, while functional substituents (-SH) at the opposite end stay extended into surrounding aqueous medium and chemically interact with heavy metal contaminates. Thiol functionalized CoFe2O4 nanoparticles were characterized using IR spectroscopy, X-ray diffraction (XRD), transmission electron microscopy/high-resolution transmission electron microscopy (TEM/HRTEM), energy-dispersive X-ray spectroscopy (EDXS) and vibrating-sample magnetometer (VSM). The thiol functionalized CoFe2O4 nanoparticles were used for Pb2+ and Hg2+ions adsorption from aqueous media. Effect of treatment has been demonstrated using atomic absorption spectroscopy (AAS).
Ključne besede: cobalt ferrite, magnetic nanoparticles, tetraethoxysilane, 3-mercaptopropyl trimetoxysilane, thiol group, lead, mercury, adsorption
Objavljeno: 02.12.2014; Ogledov: 1455; Prenosov: 91
.pdf Celotno besedilo (5,22 MB)

2.
The magnetic and colloidal properties of $CoFe_2O_4$ nanoparticles synthesized by co-precipitation
Sašo Gyergyek, Mihael Drofenik, Darko Makovec, 2014, izvirni znanstveni članek

Opis: Magnetic $CoFe_2O_4$ nanoparticles were synthesized by co-precipitation at 80 °C. This co-precipitation was achieved by the rapid addition of a strong base to an aqueous solution of cations. The investigation of the samples that were quenched at different times after the addition of the base, using transmission electron microscopy (TEM) coupled with energy-dispersive X-ray spectroscopy (EDXS) and X-ray powder diffractometry, revealed the formation of a Co-deficient amorphous phase and $Co(OH)_2$, which rapidly reacted to form small $CoFe_2O_4$ nanoparticles. The nanoparticles grew with the time of aging at elevated temperature. The colloidal suspensions of the nanoparticles were prepared in both an aqueous medium and in a non-polar organic medium, with the adsorption of citric acid and ricinoleic acid on the nanoparticles, respectively. The measurements of the room-temperature magnetization revealed the ferrimagnetic state of the $CoFe_2O_4$ nanoparticles, while their suspensions displayed superparamagnetic behaviour.
Ključne besede: cobalt ferrite, nanoparticles, co-precipitation, colloidal suspensions, magnetic properties
Objavljeno: 30.08.2017; Ogledov: 495; Prenosov: 39
.pdf Celotno besedilo (279,23 KB)
Gradivo ima več datotek! Več...

Iskanje izvedeno v 0.07 sek.
Na vrh
Logotipi partnerjev Univerza v Mariboru Univerza v Ljubljani Univerza na Primorskem Univerza v Novi Gorici