Microstructure, mechanical properties and fatigue behaviour of a new high-strength aluminium alloy AA 6086
Franc Zupanič, Jernej Klemenc, Matej Steinacher, Srečko Glodež, 2023, izvirni znanstveni članek

Opis: This study presents the comprehensive experimental investigation of the microstructure, mechanical and fatigue properties of a new high-strength aluminium alloy AA 6086, which was developed from a commercial aluminium alloy AA 6082. The new alloy possesses a higher content of Si, and, it also contains Cu and Zr. The alloy was characterised in the as-cast condition after homogenisation, extrusion, and T6 heat treatment. Light microscopy, scanning and transmission electron microscopy with energy dispersive spectrometry were used to analyse the microstructure and the fractography of broken specimens. The quasi-static and fatigue tests were performed on the MTS Landmark 100 kN servo-hydraulic test machine, controlled with a mechanical extensometer with a 25 mm gauge length. The quasi-static strength of the analysed aluminium alloy AA 6086 was found to be significantly higher if compared to some other AA 6xxx alloys, while the ductility was kept almost the same. The experimental results of the comprehensive fatigue tests in a Low Cycle Fatigue (LCF) and High Cycle Fatigue (HCF) regime showed a good fatigue resistance, and represent a good basis for engineering design applications of the newly developed aluminium alloy AA 6086.
Ključne besede: aluminijeve zlitine, karakterizacija materiala, utrujanje, eksperimentalno testiranje, statistično ovrednotenje, Aluminium Alloy AA 6086, material characterisation, fatigue behaviour, experimental testing, statistical evaluation
Objavljeno v DKUM: 02.04.2024; Ogledov: 167; Prenosov: 12
URL Povezava na celotno besedilo
Gradivo ima več datotek! Več...

3.
Preparation and electrochemical characterization of aluminium liquid battery cells with two different electrolytes ($NaCl-BaCl_2-AlF_3-NaF$ and $LiF-AlF_3-BaF_2$)
Viktor Napast, Jože Moškon, Marko Homšak, Aljana Petek, Miran Gaberšček, 2015, izvirni znanstveni članek

Opis: The possibility of preparation of operating rechargeable liquid battery cells based on aluminium and its alloys is systematically checked. In all cases we started from aluminium as the negative electrode whereas as the positive electrode three different metals were tested: $Pb$, $Bi$, and $Sn$. Two types of electrolytes were selected: $Na_3AlF_6-AlF_3-BaCl_2-NaCl$ and $Li_3AlF_3-BaF_2$. We show that some of these combinations allowed efficient separation of individual liquid layers. The cells exhibited expected voltages, relatively high current densities and could be charged and discharged several times. The capacities were relatively low (120 mAh in the case of $Al-Pb$ system), mostly due to unoptimised cell construction. Improvements in various directions are possible, especially by hermetically sealing the cells thus preventing salt evaporation. Similarly, solubility of aluminium in alloys can be increased by optimising the composition of positive electrode.
Ključne besede: liquid batteries, aluminium, alloy, electrochemistry
Objavljeno v DKUM: 24.08.2017; Ogledov: 1326; Prenosov: 333
.pdf Celotno besedilo (316,77 KB)
Gradivo ima več datotek! Več...

Iskanje izvedeno v 0.1 sek.
Na vrh
Logotipi partnerjev Univerza v Mariboru Univerza v Ljubljani Univerza na Primorskem Univerza v Novi Gorici