1.
Synthesis of NiTi/Ni-TiO[sub]2 composite nanoparticles via ultrasonic spray pyrolysis
Peter Majerič, Rebeka Rudolf, Ivan Anžel, Jelena Bogovic, Srečko Stopić, Bernd Friedrich, 2015, izvirni znanstveni članek

Opis: In this paper we present the production of NiTi/Ni-TiO2 composite nanoparticles via the synthesis method called ultrasonic spray pyrolysis (USP). The precursor solution for the synthesis of spherical NiTi particles was prepared from an orthodontic wire with a chemical composition of Ni (amount fraction x = 51.46 %) and Ti (x = 48.54 %). TEM microscopy, in combination with EDX analyses, was used for a detailed characterization of the obtained NiTi nanoparticles. The results showed the nanoparticle sizes ranging from 60 nm to 600 nm, depending on the parameters of the production procedure. This showed the versatility of the new USP synthesis procedure, proving its usefulness for different materials and applications.
Ključne besede: ultrasonic spray pyrolysis, NiTi/Ni-TiO2 composite nanoparticles, characterization, Transmission electron microscope (TEM), TEM microscopy
Objavljeno: 23.03.2017; Ogledov: 620; Prenosov: 75
.pdf Celotno besedilo (1,13 MB)
Gradivo ima več datotek! Več...