Factors influencing the yielding constraint by cracked welded components
Dražan Kozak, Jelena Vojvodič-Tuma, Nenad Gubeljak, Damir Semenski, 2005, izvirni znanstveni članek

Opis: The effect of strength mismatch for welded joints performed with different geometries on the yielding constraint has been investigated in the context of single-edged fracture-toughness specimens subjected to bending SE(B) using the finite-element method. The crack was located in the centre of the weld. Two geometri cal parameters have been identified as being the most important: the crack-Iength ratio a/W and the sIenderness of the welded joint (W-a)/H. They were systematically varied as follows: a/W = 0.1; 0.2; 0.3; 0.4; 0.5 and W = 2H, 4H, 8H, 16H, 24H. Basic equations and plane-strain finite-element solutions for the overmatched SE(B) specimen with all configuration combinations are given. The results are in good agreement with those in literature. This paper aims to establish yield-Ioad solutions for the same weldment configurations, but with materials dissimilarity present within the weld. This situation is usually encountered during repair welding. For this purpose, a practical combination of filler materials, with the same portion of overmatched part with M = 1.19 and undermatched part with M = 0.86, has been selected. Plane-strain solutions for the heterogeneous weld with the cracklocated in the overmatched half were obtained. The influence of the yielding-constraint key parameters has al so been evaluated. Yield-Ioad results for the specimens performed with different weld widths have the greatest scattering for the a/W = 0.5. The transition from the overmatched to the undermatched solution with increasing H is evident. On the other hand, the behaviour of the specimen with a shallow crack is dictated by the overmatch region ahead of the crack tip and depends very little on the weld slenderness. An approximated 3-D area of the yield-Ioad solutions depending ona/W and (W-a)lH has been proposed. Furthermore, the stress triaxility parameter h has been calculated using 2-D and 3-D finite-element analysis, and given as a field in the spec imen to get an insight into yielding-constraint regions. It was found that the 3-D yield-Ioad solutions are very close to the plane-strain solutions. Also, the effect of a/W on the yielding constraint is more significant than the effect of Mand (W-a)/H.
Ključne besede: welded structures, welded joints, fracture mechanics, cracks, SE(B) specimens, yielding load, yielding constraint parameters
Objavljeno v DKUM: 06.04.2017; Ogledov: 1488; Prenosov: 120