1.
Hydroxylammonium fluorogermanates
Irena Ban, Matjaž Kristl, Mihael Drofenik, Arkadije Popović, 2004, izvirni znanstveni članek

Opis: A new hydroxylammonium compound (NH3OH)2GeF6, has been synthesized by the addition of solid NH3OHF to a solution of GeO2 dissolved in 20% HF. The compound was characterized by chemical analysis and X-ray powder diffraction, the thermal decomposition was studied by thermal analysis and mass spectrometry. (NH3OH)2GeF6 crystallizes monoclinic. Two endothermic and two exothermic peaks have been observed on the DSC curve, the decomposition product at 500 °C is GeO2.
Ključne besede: inorganic chemistry, synthesis, characterisation, hydroxylammonium fluorogermanates, x-ray powder diffraction, mass spectroscopy, thermal analysis
Objavljeno: 01.06.2012; Ogledov: 1386; Prenosov: 43
URL Povezava na celotno besedilo

2.
Comparison of NiTi orthodontic archwires and a determination of the charasteristic properties
Janko Ferčec, Matija Kos, Mihael Brunčko, Ivan Anžel, Branislav Glišić, Evgenija Marković, Rebeka Rudolf, 2014, izvirni znanstveni članek

Opis: The aim of this paper was to analyse the characteristic properties of six different, commercially available nickel-titaniumorthodontic wires with a diameter of 0.305 mm (0.014"). The characteristic properties were determined by usingsemi-quantitative EDX analyses, DSC analyses for a determination of the phase temperatures, and a tensile test to obtain themechanical properties of the wires. The investigation of the chemical composition showed an equiatomic NiTi alloy. Analysesof phase temperatures showed that the nickel-titanium orthodontic wires were, in an austenitic microstructure, exhibiting asuperelastic effect in the oral environment. The uniaxial tensile stressstrain curves showed different values for the beginningand the end of the transformation range during the loading.
Ključne besede: shape-memory alloy, phase transformation, thermal analysis, tensile test
Objavljeno: 21.12.2015; Ogledov: 435; Prenosov: 33
.pdf Celotno besedilo (429,57 KB)
Gradivo ima več datotek! Več...

3.
Numerical analysis of temperature field during hardfacing process and comparison with experimental results
Vukić Lazić, Ivana Ivanović, Aleksandar Sedmak, Rebeka Rudolf, Mirjana Lazić, Zoran Radaković, 2014, izvirni znanstveni članek

Opis: The three-dimensional transient nonlinear thermal analysis of the hard facing process is performed by using the finite element method. The simulations were executed on the open source Salome platform using the open source finite element solver Code Aster. The Gaussian double ellipsoid was selected in order to enable greater possibilities for the calculation of the moving heat source. The numerical results were compared with available experimental results.
Ključne besede: welding simulations, numerical analysis, thermal analysis, simulations, transient heat conduction, moving heat source
Objavljeno: 07.07.2017; Ogledov: 258; Prenosov: 189
.pdf Celotno besedilo (975,43 KB)
Gradivo ima več datotek! Več...

4.
Ammoniumbis(hydroxylammonium) pentafluoridooxidovanadate(IV)
Brina Dojer, Matjaž Kristl, Zvonko Jagličić, Mihael Drofenik, Anton Meden, 2008, izvirni znanstveni članek

Opis: Turquoise crystals of a new hydroxylammonium compound with the formula $NH_4(NH_3OH)_2[VOF_5]$ have been synthesized by the reaction of solid $NH_3OHF$ and the aqueous solution of vanadium in HF. The compound crystallizes monoclinic, $P2_1/n$, with cell parameters: a = 10.5658(2) Å, b = 6.6143(1) Å, c = 11.6618(2) Å, β = 96.282(1). Magnetic susceptibility was measured using a SQUID device over a temperature range 2–300 K at magnetic field $10^3 Oe$ giving the result $µ_{eff}$ = 1.65 BM. The thermal decomposition was studied by TG and DSC analysis. $NH_4(NH_3OH)_2[OF_5V]$ decomposes above 354 K in three steps, obtaining $NH_4VOF_3$ after the first step and $V_2O_5$ as the final residue.
Ključne besede: hydroxylammonium fluorovanadates, x-ray powder diffraction, x-ray structure determination, thermal analysis
Objavljeno: 17.08.2017; Ogledov: 337; Prenosov: 36
.pdf Celotno besedilo (218,95 KB)
Gradivo ima več datotek! Več...

5.
Synthesis, crystal structure and magnetic properties of a new hydroxylammonium fluoroferrate
Brina Dojer, Matjaž Kristl, Zvonko Jagličić, Amalija Golobič, Marta Kasunič, Mihael Drofenik, 2012, izvirni znanstveni članek

Opis: This paper reports on the synthesis of a new hydroxylammonium fluoroferrate, with the formula $(NH_3OH)_3FeF_6$, obtained after dissolving iron powder in hydrofluoric acid and adding solid $NH_3OHF$. This new compound has been characterized by chemical and thermal analysis, single-crystal X-ray diffraction, and magnetic measurements. The title compound crystallizes trigonal, R3c, with cell parameters a = 11.4154(2) Å, c = 11.5720(2) Å, Z = 6. The structure consists of $NH_3OH^+$ cations and isolated $FeF_6^{3–}$ octahedra in which the central ion lies on a threefold axis. The oxygen and nitrogen atoms of the hydroxylammonium cations are donors of hydrogen bonds to fluoride anions, resulting in a network of hydrogen bonds between counterions. The effective magnetic moment $µ_{eff}$ = 5.8 BM was calculated and perfectly matches the expected value of high-spin Fe(III) ions. The thermal decomposition of the compound was studied by TG, DSC, and X-ray powder diffraction.
Ključne besede: inorganic chemistry, crystallography, coordination compounds, synthesis, crystal structure, characterization of compounds, determination of the structure of compounds, X-ray diffraction, magnetic measurements, thermal analysis, TG, DSC, hydrogen bond, metal complexes, hydroxylammonium fluoromethalatehydroxylammonium, fluoroferrate
Objavljeno: 25.08.2017; Ogledov: 545; Prenosov: 27
.pdf Celotno besedilo (198,42 KB)
Gradivo ima več datotek! Več...