1.
Assessment of the Capability of Magnetic Nanoparticles to Recover Neodymium Ions from Aqueous Solution
Ana Ambrož, Irena Ban, Thomas Luxbacher, 2022, izvirni znanstveni članek

Opis: Magnetic nanoparticles (MNPs) have received increasing attention for various applications due to their fast synthesis, versatile functionalization, and recyclability by the application of a magnetic field. The high surface-to-volume ratio of MNP dispersions has suggested their use as an adsorbent for the removal of heavy metal ions. We investigated the applicability of MNPs composed of a maghemite core surrounded by a silica shell functionalized with aminopropylsilane, γ-Fe2O3-NH4OH@SiO2(APTMS), for the removal of neodymium ions (Nd3+) from aqueous solution. The MNPs were characterized for their size, composition, surface functionality and charge. Despite of the promising properties of MNPs, their removal from the aqueous dispersion with an external magnet was not sufficient to reliably quantify the adsorption of Nd3+ by UV-Vis spectroscopy.
Ključne besede: rare earth elements, maghemite, nanoparticles, UV-Vis spectroscopy, adsorption
Objavljeno v DKUM: 08.08.2023; Ogledov: 339; Prenosov: 20
.pdf Celotno besedilo (829,86 KB)
Gradivo ima več datotek! Več...

2.
Removal of neodymium ions from aqueous solution by magnetic nanoparticles : magistrsko delo
Ana Ambrož, 2021, magistrsko delo

Opis: This work is focused on the synthesis and characterization of surface-functionalized γ-Fe2O3-NH4OH@SiO2(APTMS) nanoparticles, their applications, and performance for Nd3+ removal from aqueous solutions, with an emphasis on the characterization of MNPs and Nd(NO3)3•6H2O. The γ-Fe2O3 nanoparticles were obtained by the co-precipitation method, stabilized with ammonia solution, and functionalized by SiO2 and APTMS. Neodymium nitrate hexahydrate (Nd(NO3)3•6H2O) used in aqueous solution was synthesised from neodymium oxide (Nd2O3) powder. The thermal behaviour and stability of the magnetic nanoparticles and Nd(NO3)3•6H2O was studied with thermogravimetric analysis (TGA) in O2, N2, and air atmosphere. Transmission electron microscopy (TEM) images were obtained in order to analyse the particle morphology and measure the size distribution of the nanoparticles. The hydrodynamic diameter of particles and the zeta potential were measured to determine the stability of particles in the solution. ATR-FTIR spectroscopy was used to confirm the functionalization of the magnetic nanoparticles and the adsorption of Nd3+ ions. The effect of the REE adsorption on the MNPs was studied by comparing the sample’s UV-Vis absorption spectra. The laboratory testing and analysis of the results indicate promising applications for the removal of the REE from aqueous solutions with magnetic nanoparticles. However, the coating of the MNP core by SiO2(APTMS) is inefficient for the removal of Nd3+ ions.
Ključne besede: Magnetic nanoparticles, Rare earth elements, Neodymium, Adsorption, Zeta potential, UV-Vis spectroscopy
Objavljeno v DKUM: 03.05.2021; Ogledov: 1379; Prenosov: 155
.pdf Celotno besedilo (2,51 MB)