Atrazine removal by covalent bonding to piperazine functionalized PolyHIPEs
Irena Pulko, Mitja Kolar, Peter Krajnc, 2007, izvirni znanstveni članek

Opis: The removal of atrazine from water by a solid phase extraction technique usinginsoluble polymers is described. Porous crosslinked polymers bearing piperazine moieties were prepared in a one step reaction from the precursor 4-nitrophenylacrylate incorporating polymers (PolyHIPE type prepared by the polymerization of the continuous phase of a high internal phase emulsion and polymer beads prepared by suspension polymerization). Polymers were applied tosequester atrazine from aqueous solutions with a concentration of 33 ppb andirreversible covalent bonding to the polymers was achieved. GC/MS/MS was used to monitor the dynamics of atrazine uptake and it was found that almost complete removal of atrazine was acomplished with an excess of polymer after 48 hours at room temperature. For comparison, polymer beads of identical chemistry but lower porosity were also used and showed significantly slower action (near complete removal after 72 hours).
Ključne besede: polymer supports, polymer scavengers, monoliths, emulsion polymerisation, solid-phase synthesis
Objavljeno v DKUM: 31.05.2012; Ogledov: 2537; Prenosov: 103
URL Povezava na celotno besedilo

2.
Aryl acrylate porous functional polymer supports from water-in-oil-in-water multiple emulsions
Dejan Štefanec, Peter Krajnc, 2007, izvirni znanstveni članek

Opis: Porous functional polymer supports are a class of material of wide interest due to the possibility of immobilising reactive species. A simplified procedure was applied for the preparation of porous polymer supports using a water-in-oil-in-water multiple emulsion. The primary emulsion was a high internal phase emulsion, having a volume fraction of water phase up to 95%. Two reactive acrylates, namely 4-nitrophenyl acrylate and 2,4,6-trichlorophenyl acrylate, were (separately) incorporated in the oil phase in order to obtain porous reactive polymer supports. Both acrylates were crosslinked with either divinylbenzene or ethylene glycol dimethacrylate, and beads of size ca 60 m were obtained after the polymerisation of droplets suspended into the secondary aqueous phase. In the case of 4-nitrophenyl acrylate and divinylbenzene as a crosslinker, particles with a star shape, the core being ca 60 m in diameter and the arms ca 180 m in length, were obtained. The polymers were functionalised with morpholine, tris(2-aminoethyl)amine, piperidine or piperazine yielding supports with loadings of reactive groups of between 2.6 and 6.6 mmol g-1. The results show that multiple emulsions can be precursors for porous polymer preparation.
Ključne besede: multiple emulzije, polimerni nosilci, HIPE, organska sinteza na trdni fazi, polimerni lovilci, emulzija z visokim deležem notranje faze, aril akrilati, multiple emulsions, polymer supports, HIPE, solid phase organic synthesis, polymer supported scavengers, high internal phase emulsions, arylacrylates
Objavljeno v DKUM: 31.05.2012; Ogledov: 2849; Prenosov: 114