Iskanje po katalogu digitalne knjižnice

Opis: The main aim of this thesis was development of thin functional layers from hemicelluloses xylans on the polyethylene terephthalate (PET) surfaces. Hemicelluloses, xylans, as renewable polymers, were chemically modified in order to introduce anionic and cationic functional groups. Two types of chemical modifications were performed: carboxymethylation in order to increase anionic nature of xylans and improve their hydrophilic character and cationization for introducing of amino groups and antimicrobial characteristics. Both types of modifications were successful, which was proved by ATR FTIR and raman techniques, elemental analysis, total bound nitrogen determination, size exclusion chromatography and polyelectrolyte titrations. Polyelectrolyte titration results showed increased amounts of deprotonated carboxyl groups in carboxymethylated xylans as well as increased amounts of protonated groups in cationized xylans. Antimicrobial activity of xylans was investigated by the determination of minimal inhibitory concentration (MIC) against S. aureus, E. coli, and C. albicans and it was found out that the samples with higher amounts of active amino groups showed lower MIC. Cationised glucuronoxylan showed significantly higher antimicrobial activities against S. aureus in comparison to cationised arabinoxylan and nonmodified xylan samples. However, none of xylan samples was active against fungi. In order to analyze surface properties of solid surfaces, films from xylan (nonmodified and modified) water solution was formed by casting method. The surface chemical composition of films were investigated by x-ray photoelectron spectroscopy (XPS), and the results showed that films made from carboxymethylated xylans had significantly higher amounts of carbon fraction involved in O=C-O bonds, compared to nonmodified xylans. Such surface chemical structure caused higher surface free energy with higher electron-donor contribution and thus high hydrophilicity of these films. Films made by cationized xylans had higher amount of carbon involved in C-C and C-H bonds compared to nonmodified and lower surface free energy with increase of dispersive Lifshitz Van der Waals contribution. In order to thoroughly investigate the adsorption of xylans onto synthetic surfaces Quartz crystal microbalance with dissipation unit (QCM-D) was used. For these measurements model films were prepared from PET by spin coating technique. Adsorption studies were performed at different conditions, such as pH, concentration and ionic strength of xylan solutions. For all the chemically modified xylans the adsorption was improved at pH 5 and with increased ionic strength with divalent ions. The adsorption increased as well with increasing of xylan solution concentration. In order to improve binding of adsorbed xylans so-called anchoring polymers were applied. When anchoring polymers were applied, better adsorption and fixation of adsorbed layer was confirmed, thus the adsorbed masses of xylans after rinsing with water were significantly higher in comparison to the adsorption without immediate anchoring layer. On the basis of these results, real PET fabric surfaces were treated using chemically modified xylans. The xylan solutions were applied onto PET fabric samples using spray coating technique, which is the best approximate to the large-scale procedures. In the first step, PET fabric was activated by alkaline hydrolysis and after that, anchoring agents and carboxymethylated and/or cationized xylans were adsorbed. The success of these treatments was evaluated by the determination of negative and positive charge of the treated PET fabric samples by titration techniques, methylene blue and acid orange 7 adsorption methods, water contact angles and wettability determination. From the potentiometric titrations results it was clearly seen that each new adsorbed layer onto PET fabric totally screened the charge of the former one. FESEM images showed rather thick layers covering the
Ključne besede: hemicellulose, polyethylene terephthalate, glucuronoxylan, arabinoxylan, carboxymethylation, cationization, PET model films, quartz crystal microbalance, PET fabric, surface free energy, wettability, antimicrobial properties
Objavljeno v DKUM: 11.03.2016; Ogledov: 2333; Prenosov: 156
Celotno besedilo (4,53 MB)