Opis: Corrosion of AISI 304L stainless steel in aqueous solutions of 0.5 M $H_2SO_4$ + 0.01 M KCNS + x M NaCl was studied at different temperatures (25, 40, and 50 °C). The critical ion ($Cl^-$) concentration (CIC) and the critical pitting corrosion temperature (CPT) were determined on the basis of characteristic corrosion parameters ($i_{crit}$, $i_{pass}$, $E_{pp}$), which were obtained through potentiodynamic scanning experiments. The activation energy of the process wasfound to be equal to -42.0 (1 ± 0.08 ) kJ $mol^{-1}$. As the temperature increased, the pitting potential, $E_{pp}$, was shifted towards more negative values linearly with the reciprocal of temperature, when the concentration of added NaCl was above the CIC. In contrast, at concentrations very close to the CIC, the straight lines changed slopes. This result may indicate of the approximate boundary between metastable pitting and the beginning of stable pitting.
Ključne besede: austenitic stainless steel, critical ion ($Cl^-$) concetration, critical pitting corrosion temperature, metastable pitting
Objavljeno v DKUM: 10.07.2015; Ogledov: 1233; Prenosov: 111
Celotno besedilo (334,40 KB)
Gradivo ima več datotek! Več...

Opis: A two-dimensional computational model for simulation of contact fatigue of gear teeth flanks is presented. In the model, it is assumed that the initial crack of length 0.015 mm is initiated at the surface due to previous mechanical or heat treatment of the material as well as a consequence of the running in process. The discretized model with the initial crack is then subjected to normal contact pressure, which takes into account the elasto-hydro-dynamic (EHD) lubrication conditions, and tangential loading due to friction between contacting surfaces. The model also considers the moving contact of gear flanks, fluid trapped in the crack and residual stresses due to heat treatment of the material on crack propagation. The virtual crack extension (VCE) method, implemented in the finite element method, is then usedfor simulating the fatigue crack growth from the initial crack up to the formation of the surface pit. The computational results show that the initial surface crack of length 15 m and the considered boundary conditions lead to the appearance of very small surface pits, which can be termed as micro-pitting on gear teeth flanks. The numerical results correspond well withavailable experimental data.
Ključne besede: machine elements, gearing, fracture mechanics, numerical analysis, micro pitting, pitting simulation, matematical model, fatigue, contact mechanics, crack propagation
Objavljeno v DKUM: 01.06.2012; Ogledov: 2660; Prenosov: 0

Opis: The paper describes a general computational model for simulation of surface pitting of mechanical elements subjected to contact loading conditions. In the model it is assumed that the initial crack of length 0.015 mm is initiated at the contacting surfaces due to previously thermal, mechanical treatment of the material or running in process. The discretised model with the initial crack is then subjected to normal contact pressure, which takes into account the EHD lubrication conditions and tangential loading due to friction between contacting surfaces. The model accounts also for the influence of fluid trapped in the crack on crack prppagation. The virtual crack extension VCE method within FEM analysis is then used for 2 dimensional simulation of fatigue crack propagation from the initial crack up to the formation of the surface pit. The pit shapes and relationships between the stress intensity factor and crack length are determined for various combinations of contacting surface curvatures and loadings. The comparison of computational and available experimental results shows that the proposed model reliably simulates the surface fatigue crack growth under contact loading and can be used for computational predictions of surface pitting for various contacting mechanical elements.
Ključne besede: machine elements, gears, contact problems, pitting, fatigue crack growth, simulation, model
Objavljeno v DKUM: 01.06.2012; Ogledov: 2182; Prenosov: 111
Povezava na celotno besedilo

Opis: A computational model for simulation of surface and subsurface initiated fatigue crack growth due to contact loading is presented. The model is based on fracture mechanics theory where the required materials properties are obtained from common fatigue tests. For computational simulations an equivalent model of two contacting cylinders is used instead of simulating theactual contact of mechanical elements. The discretised model with the initial crack on or under the surface is then subjected to normal contact pressure, which takes into account the EHD-lubrication conditions, and tangential loading due to friction between contacting surfaces. The model considers also the moving contact of mechanical elements and for the surface initiated crack also the fluid trapped in the crack. The virtual crack extension method, implemented in the finite element method is then used for simulating the fatigue crack growth from the initial crack up to the formationof the surface pit. The numerical results correspond well with available experimental data. The described model can be used for simulation ofpitting phenomenon of contacting mechanical elements like gears, bearings, wheels, etc.
Ključne besede: fracture mechnaics, machine elements, gears, contact fatigue, pitting, subsurface crack initiation, computational analysis
Objavljeno v DKUM: 31.05.2012; Ogledov: 2353; Prenosov: 114
Povezava na celotno besedilo