Evaluation of the impact and fracture toughness of a nanostructured bainitic steel with low retained austenite content
Mihael Brunčko, Peter Kirbiš, Ivan Anžel, Leo Gusel, Darja Feizpour, Tomaž Irgolič, Tomaž Vuherer, 2023, izvirni znanstveni članek

Opis: The impact and fracture toughness of a nanostructured, kinetically activated bainitic steel was determined using Standard methods. Prior to testing, the steel was quenched in oil and aged naturally for a period of 10 days in order to obtain a fully bainitic microstructure with a retained austenite content below 1%, resulting in a high hardness of 62HRC. The high hardness originated from the very fine microstructure of bainitic ferrite plates formed at low temperatures. It was determined that the impact toughness of the steel in the fully aged condition improved remarkably, whereas the fracture toughness was in line with expectations based on the extrapolated data available in the literature. This suggests that a very fine microstructure is most beneficial to rapid loading conditions, whereas material flaws such as coarse nitrides and non-metallic inclusions are the major limitation for obtaining a high fracture toughness.
Ključne besede: evaluation of fracture toughness, impact toughness, nanostructured bainite, natural aging, low retained austenite content, kinetically activated bainite KAB
Objavljeno v DKUM: 16.02.2024; Ogledov: 301; Prenosov: 19