Aryl acrylate based high-internal-phase emulsions as precursors for reactive monolithic polymer supports
Peter Krajnc, Dejan Štefanec, Jane F. Brown, Neil R. Cameron, 2005, izvirni znanstveni članek

Opis: Water-in-oil high-internal-phase emulsions (HIPEs), containing 4-nitrophenyl acrylate and 2,4,6-trichlorophenyl acrylate as reactive monomers, were prepared and polymerized, and highly porous monolithic materials resulted. The novel materials were studied by combustion analysis, Fourier transform infrared spectroscopy scanning electron microscopy, mercury porosimetry, and N2 adsorption/desorption analysis. With both esters, cellular macroporous monolithic polymers were obtained: the use of 4-nitrophenyl acrylate resulted in a cellular material with void diameters between 3 and 7 m and approximately3-m interconnects, whereas the use of 2,4,6-trichlorophenyl acrylate yielded a foam with void diameters between 2 and 5 m, most interconnects being around 1 m. The resulting monoliths proved to be very reactive toward nucleophiles, and possibilities of functionalizing the novel polymer supports were demonstrated via reactions with amines bearing additional functional groups and via the synthesis of an acid chloride derivative. Tris(hydroxymethyl)aminomethane and tris(2-aminoethyl)amine derivatives were obtained. The hydrolysis of 4-nitrophenylacrylate removed thenitrophenyl group, yielding a monolithic acrylic acid polymer. Furthermore,functionalization to immobilized acid chloride was performed very efficiently, with more than 95% of the acid groups reacting. The measurement of the nitrogen content in 4-nitrophenyl acrylate poly(HIPE)s after various times of hydrolysis showed the influence of the total pore volume of the monolithic polymers on the velocity of the reaction, which was faster with themore porous polymer.
Ključne besede: organic chemistry, macroporous polymers, monolithic polymer supports, emulsion polymerisation, foams, functionalization of polymers, high-internal-phase emulsions
Objavljeno: 01.06.2012; Ogledov: 1204; Prenosov: 61
URL Povezava na celotno besedilo

2.
Preparation and characterization of poly(high internal phase emulsion) methacrylate monoliths and their application as separation media
Peter Krajnc, Nermina Leber, Dejan Štefanec, Sandra Kontrec, Aleš Podgornik, 2005, izvirni znanstveni članek

Opis: Poly(glycidyl methacrylate-co-ethyleneglycol dimethacrylate) monolithic supports were prepared by radical polymerisation of the continuous phase of water in oil high internal phase emulsions. Morphology of monolithic materialswas studied by scanning electron microscopy and mercury intrusion porosimetry. The ratio of phase volume and the degree of crosslinking influenced the void size and pore size distribution of resulting polymers. Void sizes between 1 and 10 m were observed and average pore sizes around 100nm. Polymers with 60, 75, 80 and 90% pore volume were prepared and even samples with highest pore volume showed good mechanical stability. They were modified to bear weak-anion exchange groups and tested on the separation of standard protein mixture containing myoglobin, conalbumine and trypsin inhibitor. Good separation was obtained in a very short time similar to the separation obtained by commercial methacrylate monoliths. However, higher dispersion was observed. Bovine serum albumin dynamic binding capacity for monolith with 90% porosity was close to 9 mg/ml.
Ključne besede: organic chemistry, methacrylate monoliths, preparation, emulsion polymerization, high porosity, high mechanical stability, polymer chromatographic supports, monolithic methacrylate supports, protein separation
Objavljeno: 01.06.2012; Ogledov: 1342; Prenosov: 25
URL Povezava na celotno besedilo

Iskanje izvedeno v 0.04 sek.
Na vrh
Logotipi partnerjev Univerza v Mariboru Univerza v Ljubljani Univerza na Primorskem Univerza v Novi Gorici