Opis: There is a need to develop new construction materials with improved mechanical performance and durability that are low-priced and have environmental benefits at the same time. This paper focuses on the rheological, mechanical, morphological, and durability properties of synthetic and steel fiber reinforced self-compacting concrete (SCC) containing 5–15% metakaolin (M) by mass as a green replacement for Portland cement. Testing of the fresh mixes included a slump-flow test, density, and porosity tests. Mechanical properties were determined through compression and flexural strength. A rapid chloride penetrability test (RCPT) and the chloride migration coefficient were used to assess the durability of the samples. A scanning electron microscope (SEM) with energy dispersion spectrometry (EDS) was used to study the concrete microstructure and the interfacial transition zone (ITZ). The results show that a combination of metakaolin and hybrid fibers has a negative effect on the flowability of SCC. In contrast, the inclusion of M and hybrid fibers has a positive effect on the compressive and flexural strength of SCC. The fracture of SCC samples without fibers was brittle and sudden, unlike the fiber-reinforced SCC samples, which could still transfer a considerable load with increasing crack mouth opening deflection. Overall, the chloride migration coefficients were reduced by up to 71% compared to the control mix. The chloride reduction is consistent with the resulting compact concrete microstructure, which exhibits a strong bond between fibers and the concrete matrix.
Ključne besede: self-compacting concrete, synthetic and steel fibers, metakaolin, rheology, mechanical properties, chloride penetration, SEM-EDS
Objavljeno v DKUM: 12.03.2025; Ogledov: 0; Prenosov: 2
Celotno besedilo (6,46 MB)
Gradivo ima več datotek! Več...

Opis: V magistrskem delu so predstavljeni metakaolin kot pucolanski material ter njegovi vplivi na beton in cementne malte v svežem in strjenem stanju. Za študij vpliva metakolina smo uporabili obstoječo literaturo, in sicer smo obravnavali:vpliv metakaolina na sveže betonske mešanice, vpliv na posed, vpliv na potrebo po zamesni vodi, vpliv na čas vezanja betonov in malt, vpliv na vsebnost por v betonu, vpliv na tlačno trdnost, vpliv na natezno trdnost, upogibno trdnost, vpliv na alkalno silikatno reakcijo, prodiranje kloridov, sulfatni napad in karbonatizacijo. V teoretičnem delu smo prikazalienega izmed alternativnih postopkov pridobivanja metakaolina ter njegove splošne fizikalne in kemijske lastnosti . V eksperimentalnem delu smo se posvetili vplivu metakaolina na tlačno in upogibno trdnost. Predstavljena je bila metodologija izvedbe eksperimenta, pri kateri smo uporabili različne masne deleže nadomestitve cementa z metakaolinom, z namenom doseči optimalen delež za izboljšanje tlačne in upogibne trdnosti. V zaključku so predstavljeni rezultati opravljenih preizkusov, ki so podani tako grafično kot tabelarično. V diskusiji smo primerjali dosežene rezultate s pričakovanimi.
Ključne besede: metakaolin, upogibni preizkus, tlačni preizkus, beton, malte
Objavljeno v DKUM: 20.06.2023; Ogledov: 499; Prenosov: 65
Celotno besedilo (3,23 MB)

Opis: Na začetku diplomskega dela se bomo dotaknili zgodovine materialov, s katerimi so gradili naši predniki. V nadaljevanju bomo razložili sistematiko delitve mineralnih veziv, ki jih poznamo danes ter predstavili nekatere njihove mehanske in fizikalne lastnosti. Nato bomo podrobneje obravnavali veziva, kot so elektrofiltrski pepel, metakaolin in naravni pucolan, ter le-te v laboratoriju zmešali, izmerili gostoto ter opravili preizkus tlačne in upogibne trdnosti. V zadnjem delu bomo vse rezultate zabeležili, jih analizirali in primerjali med seboj.
Ključne besede: beton, elektrofiltrski pepel, metakaolin, naravni pucolan, tlačna trdnost, upogibna trdnost
Objavljeno v DKUM: 21.07.2016; Ogledov: 2609; Prenosov: 153
Celotno besedilo (1,29 MB)