Opis: This paper presents a case study, examining the influence of a sharp bimaterial interface on the effective crack driving force in a fracture mechanics specimen. The inhomogeneity of the elastic modulus in linear elasticand non-hardening and hardening elastic-plastic bimaterials is considered. The interface is perpendicular to the crack plane. The material properties and the distance between the crack tip and the interface are systematically varied. The effect of the material inhomogeneity is captured in form of a quantity called "material inhomogeneity term",▫$C_inh$▫. This term can be evaluated either by a simple post-processing procedure, following a conventional finite element stress analysis, or by computing the J-integral along a contour around the interface, ▫$J_int$▫. The effective crack driving force,▫$J_tip$▫, can be determined as the sum of ▫$C_inh$▫ and the nominally applied far-field crack driving force, ▫$J_far$▫. The results show that ▫$C_inh$▫ can be accurately determined by both methods even in cases where ▫$J_tip$▫-values are inaccurate. When a crack approaches a stiff/compliant interface,▫$C_inh$▫ is positive and ▫$J_tip$▫ becomes larger than ▫$J-far$▫. A compliant/stiff transition leads to a negative ▫$C_inh$▫, and ▫J_tip$▫ becomes smaller than ▫$J_far$▫. The material inhomogeneity term, ▫$C_inh$▫, can have the same order of magnitude as ▫$J_far$▫. Based on the numerical results, the dependencies of ▫$C_inh$▫ on the material parameters and the geometry are derived. Simple expressions are obtained to estimate ▫$C_inh$▫. Ključne besede:mechanics of structures, fracture toughness, inhomogeneous materials, J-integral, crack driving force, interface, material force Objavljeno v DKUM: 01.06.2012; Ogledov: 1720; Prenosov: 34 Povezava na celotno besedilo

Opis: A material inhomogeneity in the direction of crack extension causes a difference between the near-tip crack driving force, Jtip, and the nominally applied far-field crack driving force, Jfar. This difference can be quantified by a material inhomogeneity term, Cinh, which is evaluated by a post-processing procedure to a conventional finite element stress analysis. The magnitude of the material inhomogeneity term is evaluated for cracks in an inhomogeneous welded joint made of a high-strength low-alloy steel. Both a crack proceeding from the under-matched (UM) to the over-matched (OM) and from the OM to the UM weld metal are treated. The effects of the inhomogeneity of the different material parameters (modulus of elasticity, yield strength, and strain hardening exponent) on Cinh and Jtip are systematically studied. The results demonstrate that the material inhomogeneity term is primarily influenced by the inhomogeneity of the yield strength. A crack growing towards an OM/UM interface experiences an accelerated crack growth rate or a pop-in, an UM/OM interface leads to a reduced crack growth rate or a crack arrest. The application of global assessment methods of the mismatch effect which are included in the Engineering Treatment Model (ETM) or in the Structural Integrity Assessment Procedures for European Industry (SINTAP) is discussed. Ključne besede:crack driving force, material inhomogeneity, mismatched weld, interface, J-integral, finite element modeling Objavljeno v DKUM: 31.05.2012; Ogledov: 1754; Prenosov: 88 Povezava na celotno besedilo