1.
Acrylic acid "reversed" polyHIPEs
Peter Krajnc, Dejan Štefanec, Irena Pulko, 2005, izvirni znanstveni članek

Opis: An oil-in-water high internal phase emulsion consisting of acrylic acid, water, and a crosslinker (N,N-methylene bisacrylamide) as the water phase, and toluene as the oil phase was successfully stabilised to sustain thermal initiation of radical polymerisation resulting in porous open-cellular monolithic material. The type of initiator used influenced the average pore size ranging from approx. 708 nm to approx. 1 087 nm, as determined by mercury porosimetry.
Ključne besede: hydrophilic polymers, macroporous polymers, poly (acrylic acid), polyHIPE, supports
Objavljeno: 01.06.2012; Ogledov: 1403; Prenosov: 65
URL Povezava na celotno besedilo

2.
Aryl acrylate based high-internal-phase emulsions as precursors for reactive monolithic polymer supports
Peter Krajnc, Dejan Štefanec, Jane F. Brown, Neil R. Cameron, 2005, izvirni znanstveni članek

Opis: Water-in-oil high-internal-phase emulsions (HIPEs), containing 4-nitrophenyl acrylate and 2,4,6-trichlorophenyl acrylate as reactive monomers, were prepared and polymerized, and highly porous monolithic materials resulted. The novel materials were studied by combustion analysis, Fourier transform infrared spectroscopy scanning electron microscopy, mercury porosimetry, and N2 adsorption/desorption analysis. With both esters, cellular macroporous monolithic polymers were obtained: the use of 4-nitrophenyl acrylate resulted in a cellular material with void diameters between 3 and 7 m and approximately3-m interconnects, whereas the use of 2,4,6-trichlorophenyl acrylate yielded a foam with void diameters between 2 and 5 m, most interconnects being around 1 m. The resulting monoliths proved to be very reactive toward nucleophiles, and possibilities of functionalizing the novel polymer supports were demonstrated via reactions with amines bearing additional functional groups and via the synthesis of an acid chloride derivative. Tris(hydroxymethyl)aminomethane and tris(2-aminoethyl)amine derivatives were obtained. The hydrolysis of 4-nitrophenylacrylate removed thenitrophenyl group, yielding a monolithic acrylic acid polymer. Furthermore,functionalization to immobilized acid chloride was performed very efficiently, with more than 95% of the acid groups reacting. The measurement of the nitrogen content in 4-nitrophenyl acrylate poly(HIPE)s after various times of hydrolysis showed the influence of the total pore volume of the monolithic polymers on the velocity of the reaction, which was faster with themore porous polymer.
Ključne besede: organic chemistry, macroporous polymers, monolithic polymer supports, emulsion polymerisation, foams, functionalization of polymers, high-internal-phase emulsions
Objavljeno: 01.06.2012; Ogledov: 1204; Prenosov: 61
URL Povezava na celotno besedilo

Iskanje izvedeno v 0.03 sek.
Na vrh
Logotipi partnerjev Univerza v Mariboru Univerza v Ljubljani Univerza na Primorskem Univerza v Novi Gorici