Influence of kinematic factors of friction stir welding on the characteristics of welded joints of forged plates made of EN AW 7049 A aluminium alloy
Milenko Perović, Sebastian Baloš, Dražan Kozak, Darko Bajić, Tomaž Vuherer, 2017, izvirni znanstveni članek

Opis: In this paper, the influence of rotation speed and welding speed on the impact strength, microstructure and cross section micro hardness of FSW welded joints of Al-Zn-Mg-Cu high strength aluminium alloy is studied. Rotation speed was varied from 750 min−1 to 850 min−1 and welding speed from 60 mm/min to 80 mm/min. It was found that the energy of crack propagation is up to three times higher than the energy of crack initiation. This ratio was found by testing the Charpy notched specimens taken from left and right from the weld centre, 4 mm from the notch in a direction opposite to a direction of welding. Micro hardness distribution in the nugget does not show large dissipation of value regardless if the measuring point is in the upper or lower section of the nugget. Weld microstructure characteristics and zones are clearly defined at the basis of grain size and material flow.
Ključne besede: dynamic recrystallization, friction stir welding, impact strength, micro hardness distribution
Objavljeno: 12.07.2017; Ogledov: 614; Prenosov: 285
.pdf Celotno besedilo (2,13 MB)
Gradivo ima več datotek! Več...

The fracture behaviour of global/local mis-matched weld joints provided on HSLA steels
Inoslav Rak, Nenad Gubeljak, Zdravko Praunseis, 2001, izvirni znanstveni članek

Opis: The fracture behaviour of thick section high strength steel weldments, that contain soft root passes, has been studied. Two different weld consumables with different strength mismatch (1>M>1) and fracture toughness properties in the WM have significantly increased the complexity of the mis-match effect and failure behaviour of weld joints, depending on the crack location and the thickness of the soft root layer. The aim was to explain the effect of strength heterogeneity between BM and WM and between different regions in WM (global/local mismatching). R-curves of WM and HAZ regions were also discussed. The conclusion is that the application of a welding procedure with a two-pass soft root layer, introduced for the purpose of reducing or even omitting preheating, can be recommended in mis-matched weld joints on steel grade HT80. Nevertheless, the alloying from BM, and the tempering effect of subsequent weld passes, have to be taken into account. They can cause reduction of the root region ductility and affect the local mismatch in WM and HAZ. The deterioration by providing a soft root layer can probably be reduced by a selected consumable and proper welding procedure. The final conclusion is that the application of a mismatched weld joint with a soft root layer can be recommended only if high root toughness can be provided.
Ključne besede: welding, welded joints, strength mismatching, fracture toughness, CTOD, hardness, impact toughness, HSLA steels
Objavljeno: 01.06.2012; Ogledov: 1438; Prenosov: 99
.pdf Celotno besedilo (441,77 KB)
Gradivo ima več datotek! Več...