Shapes of the icosahedral quasicrystalline phase in melt-spun ribbons
Tonica Bončina, 2013, kratki znanstveni prispevek

Opis: The shapes of icosahedral quasicrystalline (IQC) particles were determined in melt-spun ribbons of alloys based on the Al-Mn-Be alloy system. The sizes of the quasicrystalline particles ranged from a few tenths of nanometres up to 1m. Therefore, different methods were employed for characterizing their shapes: projection of quasicrystalline particles using transmission electron microscopy (TEM), cross-sections of IQCs on metallographically polished surfaces, and observation of deep-etched samples and extracted particles using a scanning electron microscope (SEM). It was discovered that icosahedral quasicrystalline particles preferentially grow in three-fold directions and have a tendency for faceting and adopting the shape of a pentagonal dodecahedron. The evolution of quasicrystalline shapes is systematically presented.
Ključne besede: Al-alloy, metallography, ribon, icosahedral quasicrystalline phase, shape, melt-spinning
Objavljeno: 10.07.2015; Ogledov: 437; Prenosov: 51
.pdf Celotno besedilo (134,69 KB)
Gradivo ima več datotek! Več...

Iskanje izvedeno v 0.03 sek.
Na vrh
Logotipi partnerjev Univerza v Mariboru Univerza v Ljubljani Univerza na Primorskem Univerza v Novi Gorici