1.
Behaviour of coarse grain heat affected zone (HAZ) during cycle loading
Tomaž Vuherer, P. O. Maruščak, Ivan Samardžić, 2012, izvirni znanstveni članek

Opis: This paper presents results of a study on martensitic coarse grain heat affected zone that can appear in welded joints. Mechanical properties of martensitic coarse grain heat affected zone and its microstructure were investigated. Special attention was given to its behaviour during the cycle loading under stress concentration. Stress concentration was similar to the one in real welds. The S-N curve and the fatigue limit were determined. The Paris curve and the threshold for crack propagating were also determined.
Ključne besede: welded joints, coarse grain HAZ, microstructure, fatigue limit, Paris curve
Objavljeno: 01.06.2012; Ogledov: 1048; Prenosov: 61
.pdf Celotno besedilo (359,02 KB)
Gradivo ima več datotek! Več...

2.
An integrity analysis of washing machine holders
Nenad Gubeljak, Matej Mejač, Jožef Predan, 2007, izvirni znanstveni članek

Opis: The paper deals with structure integrity analysis of the holder for the carrying cross of a washing machine drum. Premature fracture of the holder occurred between mechanical sustainable tests of washing machine in the factory. In order to prevent fracture, the task was to determine the reasons for premature fracture of the holder and to estimate the suitability of the new design of the holder cross. Input data for structure integriry analysis were obtained by material by mechanical testing of used materials. Stress and strain analysis of holder limit load was performed by finite element modeling of holder. Dynamic tests of holders with two different thicknesses were done on a servo-hydraulic machine in order to find dynamical strength and endurance of holder. Fracture behaviour of holders is defined as initiation and propagation of crack. The obtained behaviour confirmed that the new design of holders reduces stress concentration in the critical region. Consequently, the new holder subjected to the same dynamic load can endure a higher number of cycles until breakage. The total number of cycles overcomes industrial testing requirements.
Ključne besede: lomna mehanika, visokociklično utrujanje, preizkušanje lomne žilavosti, nosilci kadi pralnega stroja, mejna obremenitev, ocena celovitosti konstrukcije, fracture mechanics, high cycle fatigue, fracture toughness testing, washing machine holders, washing machine drums, structure integrity assessment, limit load
Objavljeno: 10.07.2015; Ogledov: 797; Prenosov: 56
.pdf Celotno besedilo (517,04 KB)
Gradivo ima več datotek! Več...

3.
Fatigue crack initiation from microstructurally small Vickers indentations
Tomaž Vuherer, Andrej Godina, Zijah Burzić, Vladimir Gliha, 2007, izvirni znanstveni članek

Opis: The resistivity of coarse grain steel against crack initiation in the presence of micro defects is discussed. Samples of material with martensitic microstructure were prepared by adequate thermal treatment. Microstructurally small Vickers indentations were used as an artificial micro defect. The compressive residual stresses are due to the irreversibility of plastic deformation. The moment of indenting enables to prepare samples with and without effects of residual stresses. The stress level for crack initiation depends on the actual indentation size. The location of initiated cracks is affected by the presence and character of residual stresses.
Ključne besede: welded joints, micro defect, coarse grain HAZ, crack initiation, crack growth, stress concentration, fatigue limit, Vickers, residual stresses
Objavljeno: 03.07.2017; Ogledov: 451; Prenosov: 73
.pdf Celotno besedilo (1,02 MB)
Gradivo ima več datotek! Več...

Iskanje izvedeno v 0.09 sek.
Na vrh
Logotipi partnerjev Univerza v Mariboru Univerza v Ljubljani Univerza na Primorskem Univerza v Novi Gorici