1.
Microstructure, mechanical properties and fatigue behaviour of a new high-strength aluminium alloy AA 6086
Franc Zupanič, Jernej Klemenc, Matej Steinacher, Srečko Glodež, 2023, izvirni znanstveni članek

Opis: This study presents the comprehensive experimental investigation of the microstructure, mechanical and fatigue properties of a new high-strength aluminium alloy AA 6086, which was developed from a commercial aluminium alloy AA 6082. The new alloy possesses a higher content of Si, and, it also contains Cu and Zr. The alloy was characterised in the as-cast condition after homogenisation, extrusion, and T6 heat treatment. Light microscopy, scanning and transmission electron microscopy with energy dispersive spectrometry were used to analyse the microstructure and the fractography of broken specimens. The quasi-static and fatigue tests were performed on the MTS Landmark 100 kN servo-hydraulic test machine, controlled with a mechanical extensometer with a 25 mm gauge length. The quasi-static strength of the analysed aluminium alloy AA 6086 was found to be significantly higher if compared to some other AA 6xxx alloys, while the ductility was kept almost the same. The experimental results of the comprehensive fatigue tests in a Low Cycle Fatigue (LCF) and High Cycle Fatigue (HCF) regime showed a good fatigue resistance, and represent a good basis for engineering design applications of the newly developed aluminium alloy AA 6086.
Ključne besede: aluminijeve zlitine, karakterizacija materiala, utrujanje, eksperimentalno testiranje, statistično ovrednotenje, Aluminium Alloy AA 6086, material characterisation, fatigue behaviour, experimental testing, statistical evaluation
Objavljeno v DKUM: 02.04.2024; Ogledov: 105; Prenosov: 7
URL Povezava na celotno besedilo
Gradivo ima več datotek! Več...

2.
LCF behaviour of high strength aluminium alloys AA 6110A and AA 6086
Jernej Klemenc, Srečko Glodež, Matej Steinacher, Franc Zupanič, 2023, izvirni znanstveni članek

Opis: The proposed research presents the comprehensive investigation of the Low Cycle Fatigue (LCF) behaviour of two high-strength aluminium alloys of series AA 6xxx: the conventional alloy AA 6110A and the newly developed alloy AA 6086. Both alloys were characterised in the as-cast condition after homogenisation, extrusion, and T6 heat treatment. The quasi-static strength and hardness of the aluminium alloy AA 6086 were found to be significantly higher if compared to the AA 6110A alloys, while the ductility was a little bit smaller. The LCF tests showed that the AA 6086 alloy is more suitable for the high-cycle fatigue regime. On the other hand, the engineering advantage of the AA 6110A alloy is only for low-cycle fatigue applications if less than 100 loading cycles are expected in the service life of the analysed structure. The fatigue cracks formed predominantly on the α-AlMnSi intermetallic particles in both alloys, and, during LCF tests, exhibited small crack propagation. The area of the fatigue crack growth was much smaller than the area of the forced fracture. At smaller amplitude strains the fatigue striations were present at the fracture surface, while, at higher amplitude strains, they were not present. The obtained experimental results represent a good basis for engineering design applications of the analysed alloys AA 6086 and AA 6110A.
Ključne besede: aluminijeve zlitine, malociklično utrujanje, eksperimentalno testiranje, fraktografija, aluminium alloys, low cycle fatigue, experimental testing, fractography
Objavljeno v DKUM: 29.03.2024; Ogledov: 79; Prenosov: 10
URL Povezava na celotno besedilo
Gradivo ima več datotek! Več...

3.
Računski model za analizo trdnosti smrekovega lesa : magistrsko delo
Jure Fakin, 2023, magistrsko delo

Opis: Čeprav je les v uporabi že od pradavnine, je splošno razumevanje njegovega mehanskega obnašanja zelo skromno. V magistrskem delu je na osnovi rezultatov izvedenih statičnih in dinamičnih tri-točkovnih upogibnih preizkusov, bil določen materialni model smrekovega lesa. Vrednosti statičnih materialnih parametrov so bile določene s postopkom inverzne določitve, ki temelji na zaporednem izvajanju numeričnih simulacij. Na osnovi rezultatov dinamičnih upogibnih preizkusov je bila določena enačba S-N krivulje, na osnovi katere je bila potrjena S-N krivulja, pridobljena z numeričnimi simulacijami. Končen rezultat je bil razvit in potrjen materialni model, s katerim je mogoče predvideti odziv komponent iz smrekovega lesa izpostavljenih statični obremenitvi in napovedati njihovo življenjsko dobo pri cikličnem utripnem obremenjevanju v tangencialni orientaciji lesnih vlaken.
Ključne besede: smrekov les, eksperimentalno testiranje, numerične simulacije, inverzna določitev materialnih parametrov, S-N krivulja.
Objavljeno v DKUM: 07.11.2023; Ogledov: 254; Prenosov: 41
.pdf Celotno besedilo (3,80 MB)

4.
Numerično in eksperimentalno preverjanje ustreznosti transportne embalaže gospodinjskih aparatov
Damijan Rupnik, 2013, magistrsko delo

Opis: V magistrskem delu sem razvil numerični model, ki je namenjen numeričnemu testiranju transportne embalaže za pečico NG3 pri preizkusu na prosti pad. Ta numerični model sem nato primerjal z eksperimentalnim testom (preizkus na prosti pad). Na osnovi pridobljenih podatkov sem nato v nadaljevanju numerični model priredil eksperimentalnemu testu. S tem sem zagotovil uporaben model za nadaljnje računalniške simulacije.
Ključne besede: transportna embalaža, računalniško modeliranje, numerični model, eksplicitna dinamična analiza, eksperimentalno testiranje, preizkus prosti pad
Objavljeno v DKUM: 03.09.2013; Ogledov: 2088; Prenosov: 165
URL Povezava na celotno besedilo

Iskanje izvedeno v 0.37 sek.
Na vrh
Logotipi partnerjev Univerza v Mariboru Univerza v Ljubljani Univerza na Primorskem Univerza v Novi Gorici