Fatigue crack initiation from microstructurally small Vickers indentations
Tomaž Vuherer, Andrej Godina, Zijah Burzić, Vladimir Gliha, 2007, izvirni znanstveni članek

Opis: The resistivity of coarse grain steel against crack initiation in the presence of micro defects is discussed. Samples of material with martensitic microstructure were prepared by adequate thermal treatment. Microstructurally small Vickers indentations were used as an artificial micro defect. The compressive residual stresses are due to the irreversibility of plastic deformation. The moment of indenting enables to prepare samples with and without effects of residual stresses. The stress level for crack initiation depends on the actual indentation size. The location of initiated cracks is affected by the presence and character of residual stresses.
Ključne besede: welded joints, micro defect, coarse grain HAZ, crack initiation, crack growth, stress concentration, fatigue limit, Vickers, residual stresses
Objavljeno: 03.07.2017; Ogledov: 763; Prenosov: 87
.pdf Celotno besedilo (1,02 MB)
Gradivo ima več datotek! Več...

2.
The effect of small flaws on the fatigue strength of HAZ at the weld toe
Vladimir Gliha, 2007, izvirni znanstveni članek

Opis: The effects of small artificial surface flaws on the fatigue strength of HAZ material are studied. The samples of coarse grain HAZ material were prepared using a welding thermal-cycle simulator. The artificial flaws were produced byindenting with a Vickers pyramid at different loads as either single indentations or as a series. The size of the flaws did not exceed the primary austenitic grain size of the material, which is the most relevant microstructural unit of carbon steels. The dependence of the experimentally determined bending fatigue strength of treated coarse grain HAZ materials on the properly evaluated size of the artificial flaws was compared with the law of long-crack propagation. The biggest flaws evaluated with the flaw-size parameter ?area ? 100 m are still small for the studied coarse grain HAZ. In further experimental work, the effects of flaw size and the effects of residual stresses should be analysed separately.
Ključne besede: welding, welded joints, coarse grained HAZ, crack initiation, flaw-size parameter, small surface flaws, stress intensity range, Vickers indentation, weld toe
Objavljeno: 31.05.2012; Ogledov: 1440; Prenosov: 92