The characterisation of nanosized nickel-zinc ferrites synthesized within reverse micelles of CTAB/1-hexanol/water microemulsion
Vuk Uskoković, Mihael Drofenik, Irena Ban, 2004, izvirni znanstveni članek

Opis: Stoichiometric nanocrystalline nickel-zinc ferrites were synthesized by a reverse micelle method following a multi-microemulsion approach. Different pH values were chosen for the alkali precipitating reaction during the synthesis of different powders. Synthesized, as-dried and subsequently calcined powders were characterized in terms of their magnetic properties. XRD analyses and specific-surface area measurements were used to determine the average particlesizes of the synthesized samples. DCS and TGA measurements were performed to reveal the phase transitions within the samples at elevated temperatures, whereas TEM was used to view and record the microstructure of the nanosized ferrite samples. A possible mechanism of the formation of the synthesized NiZn-ferrite was also discussed.
Ključne besede: magnetic materials, magnetic nanoparticles, microemulsion synthesis, nickel, iron, fine powders, Ni-Zn ferrites, reverse micelle method
Objavljeno: 01.06.2012; Ogledov: 1412; Prenosov: 23
URL Povezava na celotno besedilo

2.
Subsolidus phase equilibria and the Li[sub]5Nd[sub]4FeO[sub]10 phase in the Li[sub]2O-Nd[sub]2O[sub]3-Fe[sub]2O[sub]3 system
Irena Ban, Mihael Drofenik, Danilo Suvorov, Darko Makovec, 2005, izvirni znanstveni članek

Opis: A survey of the subsolidus phase equilibria in the system Li2O-Nd2O3-Fe2O3 wasmade at subsolidus temperatures in the range 1000-1050 °C. A ternary phase was identified. The phase is centered on Li5Nd4FeO10, with a cubic lattice a =11.9494 A. The compound melts incongruently at 1105 °C. The magnetic susceptibility was measured in the temperature range 4-300 K. The compound is paramagnetic in the temperature range 150-300 K and follows the Curie-Weiss law. At about TN = 10 K, a long-range magnetic ordering is observed.
Ključne besede: lithium ferrites, differential scanning calorimetry, thermogravimetric analysis, X-ray diffraction, magnetic properties, phase equilibrium
Objavljeno: 01.06.2012; Ogledov: 1606; Prenosov: 23
URL Povezava na celotno besedilo

Iskanje izvedeno v 0.06 sek.
Na vrh
Logotipi partnerjev Univerza v Mariboru Univerza v Ljubljani Univerza na Primorskem Univerza v Novi Gorici