Opis: The fracture behaviour of thick section high strength steel weldments, that contain soft root passes, has been studied. Two different weld consumables with different strength mismatch (1>M>1) and fracture toughness properties in the WM have significantly increased the complexity of the mis-match effect and failure behaviour of weld joints, depending on the crack location and the thickness of the soft root layer. The aim was to explain the effect of strength heterogeneity between BM and WM and between different regions in WM (global/local mismatching). R-curves of WM and HAZ regions were also discussed. The conclusion is that the application of a welding procedure with a two-pass soft root layer, introduced for the purpose of reducing or even omitting preheating, can be recommended in mis-matched weld joints on steel grade HT80. Nevertheless, the alloying from BM, and the tempering effect of subsequent weld passes, have to be taken into account. They can cause reduction of the root region ductility and affect the local mismatch in WM and HAZ. The deterioration by providing a soft root layer can probably be reduced by a selected consumable and proper welding procedure. The final conclusion is that the application of a mismatched weld joint with a soft root layer can be recommended only if high root toughness can be provided.
Ključne besede: welding, welded joints, strength mismatching, fracture toughness, CTOD, hardness, impact toughness, HSLA steels
Objavljeno v DKUM: 01.06.2012; Ogledov: 2073; Prenosov: 162
Celotno besedilo (441,77 KB)
Gradivo ima več datotek! Več...