Synthesis, crystal structure and magnetic properties of a new hydroxylammonium fluoroferrate
Brina Dojer, Matjaž Kristl, Zvonko Jagličić, Amalija Golobič, Marta Kasunič, Mihael Drofenik, 2012, izvirni znanstveni članek

Opis: This paper reports on the synthesis of a new hydroxylammonium fluoroferrate, with the formula $(NH_3OH)_3FeF_6$, obtained after dissolving iron powder in hydrofluoric acid and adding solid $NH_3OHF$. This new compound has been characterized by chemical and thermal analysis, single-crystal X-ray diffraction, and magnetic measurements. The title compound crystallizes trigonal, R3c, with cell parameters a = 11.4154(2) Å, c = 11.5720(2) Å, Z = 6. The structure consists of $NH_3OH^+$ cations and isolated $FeF_6^{3–}$ octahedra in which the central ion lies on a threefold axis. The oxygen and nitrogen atoms of the hydroxylammonium cations are donors of hydrogen bonds to fluoride anions, resulting in a network of hydrogen bonds between counterions. The effective magnetic moment $µ_{eff}$ = 5.8 BM was calculated and perfectly matches the expected value of high-spin Fe(III) ions. The thermal decomposition of the compound was studied by TG, DSC, and X-ray powder diffraction.
Ključne besede: inorganic chemistry, crystallography, coordination compounds, synthesis, crystal structure, characterization of compounds, determination of the structure of compounds, X-ray diffraction, magnetic measurements, thermal analysis, TG, DSC, hydrogen bond, metal complexes, hydroxylammonium fluoromethalatehydroxylammonium, fluoroferrate
Objavljeno: 25.08.2017; Ogledov: 1059; Prenosov: 50
.pdf Celotno besedilo (198,42 KB)
Gradivo ima več datotek! Več...

Ammoniumbis(hydroxylammonium) pentafluoridooxidovanadate(IV)
Brina Dojer, Matjaž Kristl, Zvonko Jagličić, Mihael Drofenik, Anton Meden, 2008, izvirni znanstveni članek

Opis: Turquoise crystals of a new hydroxylammonium compound with the formula $NH_4(NH_3OH)_2[VOF_5]$ have been synthesized by the reaction of solid $NH_3OHF$ and the aqueous solution of vanadium in HF. The compound crystallizes monoclinic, $P2_1/n$, with cell parameters: a = 10.5658(2) Å, b = 6.6143(1) Å, c = 11.6618(2) Å, β = 96.282(1). Magnetic susceptibility was measured using a SQUID device over a temperature range 2–300 K at magnetic field $10^3 Oe$ giving the result $µ_{eff}$ = 1.65 BM. The thermal decomposition was studied by TG and DSC analysis. $NH_4(NH_3OH)_2[OF_5V]$ decomposes above 354 K in three steps, obtaining $NH_4VOF_3$ after the first step and $V_2O_5$ as the final residue.
Ključne besede: hydroxylammonium fluorovanadates, x-ray powder diffraction, x-ray structure determination, thermal analysis
Objavljeno: 17.08.2017; Ogledov: 792; Prenosov: 66
.pdf Celotno besedilo (218,95 KB)
Gradivo ima več datotek! Več...

A facile route to the synthesis of coated maghemite nanocomposites for hyperthermia applications
Gregor Ferk, Irena Ban, Janja Stergar, Darko Makovec, Anton Hamler, Zvonko Jagličić, Mihael Drofenik, 2012, izvirni znanstveni članek

Opis: CM-dextran-covered maghemite particles for applications in magnetic hyperthermia treatments were synthesized and their physical, magnetic and morphological properties were examined. Magnetic fluids were prepared and their heating proper ies in an alternating magnetic field were studied. The results reveal that the particle size and the thickness of the carboxy-methyl-dextran (CM-dextran) coatings have a decisive influence on the heating properties: specific absorption rate (SAR). The majority of the magnetic dissipation comes from the Neel relaxation, while the Brown contribution is small. A thermal steady state at the selected temperature (42 °C) can be achieved using synthesized maghemite particles with proper particle morphology and by controlling the magnetic field intensity or the frequency.
Ključne besede: magnetic nanoparticles, hyperthermia, magnetic properties
Objavljeno: 10.07.2015; Ogledov: 1187; Prenosov: 68
.pdf Celotno besedilo (696,12 KB)
Gradivo ima več datotek! Več...