Development of an Al-Mn-Be-Cu alloy with improved quasicrystalline forming ability
Franc Zupanič, Tonica Bončina, Niko Rozman, Ivan Anžel, Werner Grogger, Christian Gspan, Ferdinand Hofer, Boštjan Markoli, 2008, izvirni znanstveni članek

Opis: An Al94Mn2Be2Cu2 cast alloy was developed displaying increased quasicrystalline formation ability at moderate cooling rates. The as-cast microstructure consisted of a mainly icosahedral phase in the Al-matrix. The microstructure remained stable during uniform heating to 580 °C and isothermalannealing at 400 °C. Most of the icosahedral phase was preserved even after 24 h annealing at 500 °C. For that reason, this alloy presents a promising basis for further development of cast Al-alloys containing quasicrystals.
Ključne besede: alluminium alloys, casting, quasicrystals, TEM, SEM
Objavljeno: 31.05.2012; Ogledov: 1160; Prenosov: 68
URL Povezava na celotno besedilo