1.
Role of residual stresses on fracture properties of under-matched butt weld
Inoslav Rak, Vladimir Gliha, 1999, original scientific article

Abstract: Under-matched weld joints were adopted for producing a penstock of 47 mm wall thickness and 4200 mm diameter, to improve the weldability. The isothermal Robertson wide plate test on the under-matched weld joints, were the allowable stress level was 0.6 of the yield stress, proved that the longitudinal stresses caused the crack propagation alog the weld joint to deviate into tough base material where it was arrested. The arrest temperature was between -10 and -20°C. The behaviour of the crack propagation was the reason to omit the thermal stress relieving of the pipe section and on circumferential weld joints executed on this side. One can always take into consideration the role of axial residual stresses when assessing whether to use, or not, under-matched weld joints in severer loaded structures.
Keywords: strjeni zvar z nižjo mejo tečenja, zaostale napetosti, potek loma, lastnosti ujetja, lomna žilavost, under-matched weld joint, residual stresses, fracture path, arrest properties, fracture toughness
Published: 10.07.2015; Views: 702; Downloads: 18
URL Link to full text

2.
Measurement of strain caused by residual stresses in a welded joint using neutron diffraction
Nenad Gubeljak, Jelena Vojvodič-Tuma, Hans-Georg Preismeyer, 1999, original scientific article

Abstract: The distribution and amount of residual stresses can significantly contrubute to the fatigue fracture behaviour of welded joints in structures. Interior residual stresses, which interact with the plane strain state, are more dangerous than residual stresses at the surface of the welded joint. If the surface of the welded joint is mechanically treated (e.g. shapering), then significant differences between the stress stated at the surface and within the volume occur. Hence, different non-destructive methods (e.g. gamma radiation, neutron diffraction) have been developed to determine strains caused by residual stresses in the volume of polycrystalline materials. However, the measurement of strains caused by residual stresses becomes difficult for large samples. In this paper the measurement procedure on a sample taken from the weld joint is presented and the effecet of residual stresses on fatigue crack propagation is assessed for low and high cycle loading fatigue.
Keywords: zaostale napetosti, zvarni spoj, neutronski lom žarkov, utrujenostno širjenje razpoke, neutron diffraction method, residual stresses, fatigue crack propagation, weld joint
Published: 10.07.2015; Views: 466; Downloads: 10
URL Link to full text

3.
Flaw acceptability assessment detected in HSLA steel weld joints
Inoslav Rak, 1999, original scientific article

Abstract: The flow size in weld joint can be determined by non destructive examination (NDE). Because of different mateials, and loading as well as because of the possible effect of corrosive environment the question arises how to assess reliably the allowable falw size in different weld joint parts. The presence of flaws is obvious but the possibilities of their revealing are limited and not always posssible. The flaw size and distribution are the essential parameters for the structure capacity of bearing under high loading the weld joint. The larger is the allowable flaw size anticipated, the safer is the welded structure, and the easiest is the detection of the flaw size by NDE methods. Thus for assessing the safety of complex loaded welded structure, machine parts or equipment life time, it is obligatory to consider the requirements of different "Fitness for Purpose" systems. The article presents the possibility of assessing the detected flaw by means of NDE if the material fracture toughness of the area where the fatigue crack tip located is known. The fatigue crack represents the severest discontinuity that can occur in a welded joint. The principles of IIW Guidance on Assessment of The Fitness for Purpose of Welded Structures - IIW/IIS-SST-1157-90 and BS PD 6493 and separately ETM that treats mis-matched weld joints are shown and used.
Keywords: zvarni spoji, dopustna velikost napake, lomna žilavost, trdnostna heterogenost, primernost za uporabo, weld joint, allowable flaw size, fracture toughness, strength mis-match, fitness for purpose
Published: 10.07.2015; Views: 659; Downloads: 7
URL Link to full text