1.
Experimental determination of fatigue parameters of high chromium steel under different loading and temperature conditions
Matej Drobne, Nenad Gubeljak, Srečko Glodež, 2014, original scientific article

Abstract: Fatigue investigation of high chromium steel (HCS) at different loading ratios (R = 0, R = -1) and different temperatures (20 °C, 600 °C) is presented in this paper. Before fatigue testing, monotonic mechanical properties (ultimate compressive and ultimate tensile strength) are determined at different temperatures, using standardized testing procedures according to DIN 50125 standard. Moreover Charpy impact tests at different temperatures were done with specimens that comply with the standard ISO 14556. Fatigue testing is performed on a servo - hydraulic testing machine with consideration of different loading conditions as described above. On the basis of the experimental results the S - N curves are constructed from which typical fatigue parameters (the fatigue strength coefficient 0'f and the fatigue strength exponent b) are determined. After fatigue testing a comprehensive investigation of fracture surfaces is performed using the Scanning Electron Microscope (SEM). Experimental results presented in this paper will serve as a basis for further investigations related to fatigue behaviour of real working rolls in hot strip mills made of HCS.
Keywords: experiments, high chromium steel, high cycle fatigue, fracture mechanics
Published: 12.07.2017; Views: 514; Downloads: 99
.pdf Full text (2,88 MB)
This document has many files! More...

2.
Fatigue crack growth and fracture mechanics analysis of a working roll surface layer material
Matej Drobne, Tomaž Vuherer, Ivan Samardžić, Srečko Glodež, 2014, original scientific article

Abstract: Fatigue crack growth and fracture mechanics analysis of a working roll surface layer material is presented in this paper. The research is done on a hot strip mill working roll where High Chromium Steel is used for roll’s shell material. To obtain corresponding parameters, a rectangular single edge notched bend specimens – SENB, according to standard BS 7448, were used. The fatigue crack growth analysis was done on a resonant testing machine with use of special crack gauges, while for fracture mechanics parameters the electro–mechanical testing machine was used.
Keywords: fracture mechanics, fatigue crack growth, metal forming, rolling process, high chromium steel
Published: 03.07.2017; Views: 491; Downloads: 81
.pdf Full text (1,11 MB)
This document has many files! More...