1.
Aryl acrylate porous functional polymer supports from water-in-oil-in-water multiple emulsions
Dejan Štefanec, Peter Krajnc, 2007, original scientific article

Abstract: Porous functional polymer supports are a class of material of wide interest due to the possibility of immobilising reactive species. A simplified procedure was applied for the preparation of porous polymer supports using a water-in-oil-in-water multiple emulsion. The primary emulsion was a high internal phase emulsion, having a volume fraction of water phase up to 95%. Two reactive acrylates, namely 4-nitrophenyl acrylate and 2,4,6-trichlorophenyl acrylate, were (separately) incorporated in the oil phase in order to obtain porous reactive polymer supports. Both acrylates were crosslinked with either divinylbenzene or ethylene glycol dimethacrylate, and beads of size ca 60 m were obtained after the polymerisation of droplets suspended into the secondary aqueous phase. In the case of 4-nitrophenyl acrylate and divinylbenzene as a crosslinker, particles with a star shape, the core being ca 60 m in diameter and the arms ca 180 m in length, were obtained. The polymers were functionalised with morpholine, tris(2-aminoethyl)amine, piperidine or piperazine yielding supports with loadings of reactive groups of between 2.6 and 6.6 mmol g-1. The results show that multiple emulsions can be precursors for porous polymer preparation.
Keywords: multiple emulzije, polimerni nosilci, HIPE, organska sinteza na trdni fazi, polimerni lovilci, emulzija z visokim deležem notranje faze, aril akrilati, multiple emulsions, polymer supports, HIPE, solid phase organic synthesis, polymer supported scavengers, high internal phase emulsions, arylacrylates
Published: 31.05.2012; Views: 1588; Downloads: 79
URL Link to full text

2.
Porozni kopolimeri iz vinilestrov in tiolov kot nosilci bioloških celic
Mateja Gojznikar, 2018, master's thesis

Abstract: Porozni polimerni materiali so vedno bolj uporabni za nanos bioloških celic in uporabo v tkivnem inženirstvu. Zato smo v magistrski nalogi pripravili porozne polimerne nosilce s pomočjo polimerizacije emulzije z visokim deležem notranje faze (HIP emulzije). Za pripravo smo izbrali nizko citotoksična monomera DVA in TT in jih ustrezno polimerizirali po principu stopenjske tiol-en foto polimerizacije. Pri pripravi HIP emulzije smo spreminjali različne parametre (količino surfaktantov, HLB vrednost surfaktantov, temperaturo vodne faze, temperaturo emulzije, razmerje monomerov) in s tem pridobili različne morfološke strukture vzorcev. Pri preučevanju vpliva dveh HLB vrednosti surfaktantov (2,31 in 3,29) in količine surfaktantov (15 vol. %, 20 vol. % in 25 vol.%), smo ugotovili, da količina surfaktanta pri posamezni HLB vrednosti vpliva na poliHIPE morfologijo in na velikost primarnih por. Pri HLB vrednosti 2,31 se s povečevanjem količine surfaktantov izboljšuje poliHIPE morfologija in nastajajo večje primarne pore. Pri HLB vrednosti 3,29 pa s povečevanjem količine surfaktantov porušimo poliHIPE morfologijo in zmanjšamo primarne pore. S spremembo temperature vodne faze na 40 °C prav tako vplivamo na morfologijo polimernega nosilca, in sicer pri večji HLB vrednosti (3,29) dobimo poliHIPE morfologijo, pri manjši HLB vrednosti (2,31) pa se izoblikuje bikontinuirna struktura. S spreminjanjem temperature emulzije nismo dosegli poliHIPE morfologije, vsi vzorci imajo bikontinuirno strukturo. Pri spreminjanju razmerja funkcionalnih skupin monomerov smo ugotovili, da primerno poliHIPE morfologijo pridobimo pri vzorcu MG7, kjer je razmerje funkcionalnih skupin monomerov 1:1. Preverili smo tudi biorazgradljivost polimernih materialov MG7 in MG8 v različnih koncentracijah NaOHaq (10-3 M, 10-4 M in 10-5 M ). Ugotovili smo, da razgradljivost pripravljenih vzorcev pada z nižanjem koncentracije NaOHaq. V 10-3 M NaOHaq se namreč razgradi 10 % vzorca, v 10-4 M NaOHaq se razgradi 6 % in v 10-5 M NaOHaq le še 3% vzorca. Opravili smo tudi karakterizacijo pripravljenih poliHIPE materialov. S FTIR spektroskopijo smo potrdili kemijsko sestavo poli(DVA-ko-TT) nosilca, s pomočjo adsorpcije/desorpcije dušika po BET metodi smo izmerili specifične površine. Izvedli smo tudi elementno analizo vzorcev, in ugotovili, da eksperimentalne vrednosti masnih deležev elementov ne odstopajo od teoretičnih vrednosti. Izmerili pa smo tudi mehanske lastnosti izbranih polimernih materialov.
Keywords: Tiol-en fotopolimerizacija, HIPE nosilci, HIP emulzija, porozni polimerni nosilci, nosilci za biološke celice.
Published: 09.10.2018; Views: 272; Downloads: 55
.pdf Full text (3,52 MB)