Search the digital library catalog

Abstract: Dentures and epitheses are mostly made from poly(methyl methacrylate) (PMMA), which does not show antimicrobial properties. They present reservoirs of microorganisms grown in biofilms. The aim of this study is to prepare a PMMA enriched with gold nanoparticles (AuNPs)- PMMA/AuNPs and the examination of its physical, mechanical and antimicrobial properties. The AuNPS were synthetized from HAuCl4 using the ultrasonic spray pyrolysis method with lyophilization. The PMMA/AuNP samples were compared to PMMA samples. Density was measured by pycnometer. Microhardness was evaluated using the Vickers hardness test. Monomicrobial biofilm formation (Streptococcus mitis, Candida albicans, Staphylococcus aureus and Escherichia coli) was measured by colony-forming units (CFUs) and MTT test and visualized by SEM. AuNP release was measured indirectly (the CFUs of the medium around the sample). The density and microhardness of the PMMA/AuNPs were similar to those of the PMMA. CFU and MTT values for the biofilms formed on the PMMA for each of the tested species were higher than those of the biofilms formed on the PMMA/AuNPs. The CFUs of the medium around the sample were similar for both materials. PMMA/AuNPs showed a significant reduction in the monomicrobial biofilms of all tested species. AuNPs are not released from PMMA/AuNPs. Density, indirect measurement of residual monomer and dentures weight were similar between PMMA and PMMA/AuNPs. Microhardness, as a measure of the wear resistance, was also similar between tested discs.
Keywords: PMMA, gold nanoparticles (AuNPs), biofilm, antibiofilm effect
Published in DKUM: 24.03.2025; Views: 0; Downloads: 2
Full text (4,99 MB)
This document has many files! More...

Abstract: Wear resistance is one of the most important physical properties of the artificial teeth used in acrylic dentures. The goal of this research was to synthesize a new composite material made of matrix Poly-(methyl methacrylate)-PMMA with different percentages (2 % and 3 % of volume fractions) of zinc-oxide nanoparticles (ZnO NPs) as reinforcing elements, to improve its mechanical properties. The dynamic mechanical behaviour of this composite was studied through the DMA method in comparison to the pure PMMA supported by the characterization of their microstructures. Then the wear resistance was analysed on the samples, which were prepared in the form of teeth. In this context their vertical height loss was measured after 100,000 chewing cycles on a chewing simulator, before and after the artificial thermal ageing. Investigations showed that the PMMA/ZnO NP composites dampened the vibrations better than the pure PMMA, which could be assigned to the homogenous distribution of ZnO NPs in the PMMA matrix. It was found that the mean vertical height loss for the pure PMMA teeth was significantly higher (more than 4 times) compared to composite teeth made with ZnO NPs. Introducing the thermal artificial ageing led to the finding that there was no effect on the height loss by the composite material with 3 % of volume fractions of ZnO NPs. Based on this it was concluded that PMMA/ZnO NPs composites showed improved in-vitro wear resistance compared to acrylic-resin denture teeth, so this new composite material should be preferred when occlusal stability is considered to be of high priority.
Keywords: poly-methyl methacrylate, PMMA, zinc-oxide nanoparticles, composite, resin teeth
Published in DKUM: 12.12.2017; Views: 1876; Downloads: 448
Full text (1,55 MB)
This document has many files! More...