Abstract: An Al94Mn2Be2Cu2 cast alloy was developed displaying increased quasicrystalline formation ability at moderate cooling rates. The as-cast microstructure consisted of a mainly icosahedral phase in the Al-matrix. The microstructure remained stable during uniform heating to 580 °C and isothermalannealing at 400 °C. Most of the icosahedral phase was preserved even after 24 h annealing at 500 °C. For that reason, this alloy presents a promising basis for further development of cast Al-alloys containing quasicrystals.Keywords: alluminium alloys, casting, quasicrystals, TEM, SEMPublished: 31.05.2012; Views: 1144; Downloads: 65 Link to full text
Keywords: quasicrystals, rapid solidification, microstructure, metallography, electron emission spectroscopiesPublished: 01.06.2012; Views: 1153; Downloads: 58 Link to full text