1.
Microstructure analysis of internally oxidized Cu-C composite
Rebeka Rudolf, Ladislav Kosec, Alojz Križman, Ivan Anžel, 2006, original scientific article

Abstract: On the basis of experimentally obtained data, it was established that submicron-size bubbles are formed by the internal oxidation of Cu-C composite with fine dispersed graphite particles. They are homogeneously distributed in the Cu-matrix. This process starts with the dissolution of oxygen into the metal at the free surfaces, and continues with the diffusion of oxygen atoms into the volume of copper crystal lattice where they react with the graphite particles. The reactions of dissolved oxygen with carbon yield the gas products (CO2, CO), which cannot be dissolved in the crystal lattice of the matrix. The gas molecules, which are enclosed in the space previously occupied by the graphite, have a greater specific volume than the solid graphite. Consequently, compressive stresses arise in the copper matrix around the bubbles. The interaction of these stress fields with gliding dislocations during loading could improve the mechanical properties of the copper. The internal oxidation kinetic in Cu-C composite depends on the diffusion of oxygen in the copper matrix, and the penetration depth of the internal oxidation front indicates the parabolic nature of the process.
Keywords: metallurgy, Cu-C composites, internal oxidation, bubbles
Published in DKUM: 03.07.2017; Views: 1180; Downloads: 97
.pdf Full text (1,20 MB)
This document has many files! More...

2.
Raziskave difuzijskega žarjenja pocinkanega jekla Č.5432
Franc Zupanič, Alojz Križman, 1993, original scientific article

Keywords: jekla, pocinkana jekla, difuzijsko žarjenje, trdnost
Published in DKUM: 10.07.2015; Views: 1573; Downloads: 47
URL Link to full text

3.
4.
Vpliv postopka izdelave na mikrostrukturo predzlitine Al-Ti-B
Franc Zupanič, Alojz Križman, Gorazd Lojen, Tonica Bončina, Ivan Anžel, 1995, original scientific article

Published in DKUM: 10.07.2015; Views: 912; Downloads: 43
URL Link to full text

5.
Mikrostruktura hitro strjenih trakov zlitine Cu-Zr
Ivan Anžel, Alojz Križman, Tonica Bončina, Franc Zupanič, Gorazd Lojen, L. Kosec, Borivoj Šuštaršič, 1995, original scientific article

Abstract: Hitro strjene trakove zlitin Cu -0,5% Zr in Cu - 1% Zr smo izdelali s postopkom litja taline na hitro se vrteči boben pri različnih procesnih parametrih. Mikrostrukturo trakov smo raziskali v odvisnosti od debeline oziroma povprečne ohlajevalne hitrosti in od sestave zlitin. V prečnem prerezuje mikrostruktura tankih trakov (50-55▫$mu$▫m) sestavljena iz cone transkristalnih zrn, ki sega do zgornje proste površine in v kateri ločimo tri področja z različno substrukturo: področje brez mikrosegregacij, področje trakaste substrukture in področje s celično/dendritno substrukturo. Trakovi z debelino 85-90▫$mu$▫m vsebujejo v prečnem prerezu poleg transkristalne cone še cono globularnih zrn z dendritno morfologijo. Velikost posamezne cone ter substrukturnih področij znotraj transkristalne cone je pri isti debelini trakov odvisna od kemijske sestave zlitin.
Keywords: hitro strjevanje, mikrostruktura, trakovi, Cu - Zr zlitina
Published in DKUM: 10.07.2015; Views: 1600; Downloads: 58
URL Link to full text

6.
Vpliv parametrov pri kontinuirnem litju na mehanske lastnosti zlitine Cu-Cr-Zr
Leo Gusel, 1994, original scientific article

Keywords: metalurgija
Published in DKUM: 10.07.2015; Views: 1319; Downloads: 32
URL Link to full text

7.
Disperzijsko utrjanje hitro strjene zlitine Cu-Zr
Ivan Anžel, L. Kosec, Alojz Križman, 1996, original scientific article

Abstract: Z oksidnimi delci disperzijsko utrjene bakrove zlitine se odlikujejo s kombinacijo dobre električne in toplotne prevodnosti, izboljšanimi mehanskimi lastnostmi in povečano stabilnostjo mikrostrukture pri povišanih temperaturah. Te zlitine so danes največkrat izdelane s postopkom notranje oksidacije binarnih zlitin Cu - Al z maksimalno 1,5 at.% Al, kar daje od 1-3 vol.% zelo finih disperzoidov ▫&Al_2O_3&▫. Koagulacija delcev ▫&Al_2O_3&▫ pri visokih temperaturah in velik vpliv mejne površine med matico in oksidnimi delci na njihovo sposobnost, da pri povišani temperaturi zavirajo gibanje dislokacij, narekujejo iskanje novih, primernejših delcev za disperzijsko utrjanje bakra. V prispevku predstavljamo rezultate raziskav, s katerimi smo ugotavljali možnosti doseganja drobne disperzije oksidov ▫&ZrO_2&▫ v bakrovi matici z notranjo oksidacijo hitro strjenih trakov zlitine Cu - Zr.
Published in DKUM: 10.07.2015; Views: 1652; Downloads: 86
URL Link to full text

8.
Interakcija modifikacijske zlitine AlTi5B1 s talino zlitine AlCu6PbBi
Franc Zupanič, Alojz Križman, Savo Spaić, 1996, original scientific article

Abstract: V delu je raziskan potek taljenja in raztapljanja modifikacijske zlitine AlTi5B1 v talini zlitine AlCu6PbBi ter način njenega udrobnilnega delovanja. Taljenje in raztapljanje modifikacijske zlitine se prednostno začne na mestih dobrega kontakta med modifikacijsko in osnovno zlitino ter v področjih z nizkotaljivimi mikrostrukturnimi sestavinami v modifikacijski zlitini. Med raztapljanjem difundirata titan in bor iz modifikacijske zlitine v osnovno talino, baker in drugi elementi iz zlitine AlCu6PbBi pa v nasprotni smeri. Fazi Al3Ti in (TiAl)B2, ki se nahajata v prehodni coni, se raztapljata. Med strjevanjem nastanejo enakoosna kristalna zrna matrice [alfa]Al, ki so na meji AlTi5B1/prehodna cona velika od 10 do 30mikrom ter preko 1 mm v nedotaknjeni talini AlCu6PbBi. Hkrati z naraščanjem velikosti kristalnih zrn se spreminja tudi njihova morfologija od poligonalne k dendridni. V prehodni coni, v področjih z nadperitektično koncentracijo titana, večinoma sproži kristalizacijo faza Al3Ti, medtem ko v področjih s pod peritektično vsebnostjo titana kristalizacijski centri po vsej verjetnosti delci (Ti,Al)B2.
Keywords: metalurgija, taljenje, raztapljanje, udrobnjevanje, Al-Cu, AlTi5B1
Published in DKUM: 10.07.2015; Views: 1688; Downloads: 62
URL Link to full text

9.
Vpliv procesnih parametrov pri postopku thixsocasting na mikrostrukturo zlitine AlSi7
Rebeka Rudolf, Alojz Križman, 1997, original scientific article

Abstract: Postopek thixocasting se uporablja za izdelavo nekaterih Al zlitin s posebnimi lastnostmi. Pri tem postopku se spremeni neugodna dendritna morfologija primarnih kristalov v globulitno. Uporablja se pri izdelavi proizvodov s tlačnim litjem , z utopnim kovanjem, pri izdelavi kompozitov, itd. Kot etapno nalogo pri izdelavi kompozitov na osnovi aluminijevih zlitin smo raziskovali vpliv procesnih parametrov (temperatura in hitrost mešanja) na velikost in obliko globulitnih zrn. V prispevku podajamo analizo mikrostrukture tako izdelane zlitine AlSi7. Rxziskave kažejo, da je globulitna mikrostruktura [alfa]-primarnih zmesnih kristalov močno odvisna od hitrosti mešanja in temperature v dvofaznem področju. Na končno mikrostrukturo tako izdelanega materiala pa vpliva tudi hitrost ohlajevanja s temperature dvofaznega področja do sobne temperature.
Keywords: livarstvo, tiksotropno ulivanje, AlSi zlitine, globulitna mikrostruktura
Published in DKUM: 10.07.2015; Views: 1660; Downloads: 45
URL Link to full text

10.
Visokotemperaturna stabilnost mikrostrukture hitro strjene zlitine Cu-Zr
Ivan Anžel, Alojz Križman, 1997, original scientific article

Abstract: S postopkom hitrega strjevanja lahko v zlitinskih sistemih zmanjšamo stopnjo izcejanja in velikosti zrn, ali pa dosežemo celo prenasičeno trdno raztopino. Atomizirani prahovi in hitro strjeni trakovi so v nadaljevanju procesa navadno izpostavljeni visokim temperaturam (sintranje, ekstruzija, itd.). Uporabna vrednost hitrega strjevanja je zato pri posameznem zlitinskem sistemu pogosto odvisna tudi od visokotemperaturne stabilnosti hitro strjene mikrostrukture in odpornosti delcev utrjevalne faze na rast. Z raziskavami visokotemperaturne stabilnosti mikrostrukture hitro strjenih trakov smo za zlitino Cu-Zr določili kinetiko in aktivacijsko energijo rasti delcev intermetalne faze. V prispevku predstavlejni rezultati kažejo, da je rast delcev kontrolirana z volumsko difuzijo cirkonija, in da velja zveza r3~t pri vseh raziskanih temperaturah.
Keywords: metalurgija, zlitina Cu-Zr, hitro strjevanje, Ostwaldovo zorenje
Published in DKUM: 10.07.2015; Views: 2270; Downloads: 77
URL Link to full text